Mechanical Properties of the Cured Laminates on the Hot-press Tackified Preforms in Vacuum Assisted Resin Transfer Molding
A hot-press tackified preform was used to improve the uniformity of the laminates thickness and the mechanical properties of the obtained laminates were studied using vacuum assisted resin transfer molding(VARTM). Two modified preforms were prepared under 0.1 and 0.6 MPa in an autoclave and then wer...
Saved in:
Published in | Journal of Wuhan University of Technology. Materials science edition Vol. 33; no. 1; pp. 242 - 248 |
---|---|
Main Author | |
Format | Journal Article |
Language | English |
Published |
Wuhan
Wuhan University of Technology
01.02.2018
Springer Nature B.V |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | A hot-press tackified preform was used to improve the uniformity of the laminates thickness and the mechanical properties of the obtained laminates were studied using vacuum assisted resin transfer molding(VARTM). Two modified preforms were prepared under 0.1 and 0.6 MPa in an autoclave and then were used to fabricate the laminates via VARTM. Permeability and thickness distribution of the laminates were obtained by using a special device. Moreover, the tensile and compressive strengths of the obtained laminates were studied and compared with the unmodified ones. Results show that the tackified laminates present a maximum and minimum thickness under 0.1 and 0.6 MPa, respectively. The thicknesses and in-plane permeability of the tackified laminates, with better thickness uniformity, are significantly decreased compared with that of the unmodified cases, while the tensile and compressive strengths of the tackified laminates are improved obviously. Results show that the mechanical property of the tackified laminates prepared by hotpressing at 0.1 MPa is better than that processed at 0.6 MPa. |
---|---|
Bibliography: | hot-press tackified preforms; thickness uniformity; mechanical property; permeability;VARTM 42-1680/TB A hot-press tackified preform was used to improve the uniformity of the laminates thickness and the mechanical properties of the obtained laminates were studied using vacuum assisted resin transfer molding(VARTM). Two modified preforms were prepared under 0.1 and 0.6 MPa in an autoclave and then were used to fabricate the laminates via VARTM. Permeability and thickness distribution of the laminates were obtained by using a special device. Moreover, the tensile and compressive strengths of the obtained laminates were studied and compared with the unmodified ones. Results show that the tackified laminates present a maximum and minimum thickness under 0.1 and 0.6 MPa, respectively. The thicknesses and in-plane permeability of the tackified laminates, with better thickness uniformity, are significantly decreased compared with that of the unmodified cases, while the tensile and compressive strengths of the tackified laminates are improved obviously. Results show that the mechanical property of the tackified laminates prepared by hotpressing at 0.1 MPa is better than that processed at 0.6 MPa. WANG Changehun1, YE Jinrui2, YUE Guangquan3, BAI Guanghui4, LIU Ling5, ZHANG Boming1 (1. School of Materials Science and Engineering, Beihang University, Beijing 100191, China; 2. Association for Science and Technology of Beihang University, Beijing 100191, China; 3. Beij'ing Key Laboratory of Civil Aircraft Structures and Composite Materials, Beijing Aeronautical Science & Technology Research Institute of COMAC, Beijing 102209, China; 4. Science and Technology on Space Physics Laboratory, Beijing Institute Nearspace Vehicle's System Engineering, Beijing 100076, China; 5. School of Aerospace Engineering and Applied Mechanics, Tongji University, Shanghai 200092, China) |
ISSN: | 1000-2413 1993-0437 |
DOI: | 10.1007/s11595-018-1812-1 |