Local atomic structure of chromium bearing precipitates in chromia doped uranium dioxide investigated by combined micro-beam X-ray diffraction and absorption spectroscopy
Experimental studies have evidenced the presence of some chromium oxide precipitates in chromia (Cr2O3) doped UO2 fuels, currently being used in many light water reactors. The main objective of this study was to analyze the atomic scale microstructure of these precipitates in a non-destructive way e...
Saved in:
Published in | Journal of nuclear materials Vol. 449; no. 1-3; pp. 158 - 167 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | English |
Published |
Elsevier B.V
01.06.2014
|
Online Access | Get full text |
Cover
Loading…
Summary: | Experimental studies have evidenced the presence of some chromium oxide precipitates in chromia (Cr2O3) doped UO2 fuels, currently being used in many light water reactors. The main objective of this study was to analyze the atomic scale microstructure of these precipitates in a non-destructive way employing modern synchrotron-based X-ray radiation. To investigate UO2 microstructures and chemical compositions of the precipitates an industrial grade fresh Cr2O3-doped UO2 pellet (produced with an initial amount of 0.16wt.% Cr2O3 powder) was examined using scanning electron microscopy (SEM) and electron probe micro analysis (EPMA). Average grain diameter of the UO2 matrix was measured by SEM image analysis method. Precipitates were detected by EPMA. For all precipitates of micrometer scale analyzed by EPMA the composition was determined to be very close to Cr2O3. The structural property and the next neighbor Cr atomic environment in these precipitates were studied by a combination of more sensitive tools such as micro-focused X-ray diffraction (μ-XRD) and absorption spectroscopy (μ-XAS). According to the XRD data, the chromia precipitates contain structural disorder and have a somewhat distorted lattice structure as compared to that of standard and crystalline α-Cr2O3 hexagonal crystal unit cell. The μ-XAS results provide insight into the local atomic environment of chromium including the oxidation state assignment. |
---|---|
Bibliography: | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
ISSN: | 0022-3115 1873-4820 |
DOI: | 10.1016/j.jnucmat.2014.03.017 |