Effects of pore density on microstructure and mechanical properties of porous SiC ceramic foam/Zr-based metallic glass interpenetrating phase composites

• Published in: Intermetallics Vol. 129; p. 106964
• Main Authors: Su, Xiang, Qi, Zhixiang, Qu, Hongjie, Zhang, Jinpeng, Shen, Yun, Cao, Yuede, Chen, Guang
• Format: Journal Article
• Language: English
• Published: Barking Elsevier Ltd 01.02.2021; Elsevier BV
• Subjects: Adhesive wear; Amorphous materials; Ceramics; Coefficient of friction; Composite materials; Compression tests; Compressive strength; Deformation wear; Density; Diffusion layers; Foams; Friction reduction; Mechanical properties; Metallic glasses; Microstructure; Plastic deformation; Porous materials; Pressure effects; Water quenching; Wear-resistant; Zirconium carbide; Mechanical properties; Metallic glasses; Wear-resistant; Porous materials
• ISSN: 0966-9795; 1879-0216
• DOI: 10.1016/j.intermet.2020.106964

The porous SiC ceramic foam/Zr-based metallic glass interpenetrating phase composites were prepared by water quenching after pressure infiltration. Effects of pore density on microstructure and mechanical properties of interpenetrating phase composites are reported. Microstructural investigations show that the metallic glass is completely infiltrated into the open pores of the SiC ceramic foams and a typical interconnected amorphous phase is formed. A ~10 µm thick diffusion layer in which the reactant ZrC is generated can be found between the ceramic phase and the glassy phase. The average size of the metallic glass phase decreases with increasing the pore density. The results of the quasi-static compression tests indicate that the compressive strength of the composites increases with the pore density of the SiC foams due to the formation of more high-quality interfaces. The brittle fracture of the composites is mainly attributed to the premature destruction of the SiC foams. The results of friction tests imply that compared with monolithic Zr-based BMG samples, the reinforcement of SiC retards the adhesive wear and plastic deformation of Zr-based BMG, and reduces the friction coefficient of the composites. •Both the SiC foam and the Zr-based BMG exhibit a three-dimensionally interconnected structure.•Finer and more dispersed metallic glass phase is produced and the compressivestrength of the composites increases with pore density of SiC foam.•The brittle fracture of composites is mainly attributed to the premature destruction of the porous SiC foams.•The SiC retards adhesive wear and plastic deformation of the Zr-based BMG.