Polymerization of aniline in the galleries of layered HNbMoO6
Insertion of aniline molecules and subsequent polymerization using FeCl3 as an oxidizing agent were examined in the layers of rutile-type HNbMoO6. Although the polyaniline/host ratio was variable depending on the amount of intercalated aniline before polymerization, the interlayer spacing was consta...
Saved in:
Published in | Solid state ionics Vol. 120; no. 1-4; pp. 189 - 195 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Amsterdam
Elsevier B.V
01.05.1999
Elsevier Science |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Insertion of aniline molecules and subsequent polymerization using FeCl3 as an oxidizing agent were examined in the layers of rutile-type HNbMoO6. Although the polyaniline/host ratio was variable depending on the amount of intercalated aniline before polymerization, the interlayer spacing was constant as ∼6.3 Å regardless of the ratios. Comparison of FT-IR and FT-Raman spectra for (PANI)yNbMoO6 (0.26≤y≤0.64) clearly showed that both quinoid and benzenoid forms exist in the galleries of inorganic host. IR and Raman active modes of extracted PANI from the matrix were quite similar to those of emeraldine salt. |
---|---|
ISSN: | 0167-2738 1872-7689 |
DOI: | 10.1016/S0167-2738(99)00002-8 |