A study on friction and wear characteristics of substitute chromium brush plating layers under lubrication
The chromium plating layer shows excellent wear resistance under lubrication at low speed and light load. However, its wear resistance is not very good at high speed and heavy load. The newly developed substitute chromium brush plating layer behaves satisfactorily under both sets of conditions. Fric...
Saved in:
Published in | Wear Vol. 167; no. 2; pp. 127 - 131 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | English |
Published |
Elsevier B.V
02.08.1993
|
Online Access | Get full text |
Cover
Loading…
Summary: | The chromium plating layer shows excellent wear resistance under lubrication at low speed and light load. However, its wear resistance is not very good at high speed and heavy load. The newly developed substitute chromium brush plating layer behaves satisfactorily under both sets of conditions. Friction and wear tests were conducted and average and flash temperatures of substitute chromium plating layer were calculated. The microstructures of plating layer before and after the wear process were analysed by SEM, AES and XPS. The mechanism of its excellent wear resistance at high speed and heavy load is described. |
---|---|
Bibliography: | ObjectType-Article-2 SourceType-Scholarly Journals-1 ObjectType-Feature-1 content type line 23 |
ISSN: | 0043-1648 1873-2577 |
DOI: | 10.1016/0043-1648(93)90317-F |