Alloy optimization for PWR steam generator heat-transfer tubing
Persistent issues of corrosion degradation, both on the tubing inner diameter (ID) [primary water stress corrosion cracking (PWSCC)] and OD [intergranular attack (IGA) and stress corrosion cracking (SCC)] surfaces led to efforts to optimize the metallurgical characteristics of Alloy 600.1,2 The init...
Saved in:
Published in | JOM (1989) Vol. 53; no. 7; pp. 14 - 17 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | English |
Published |
New York
Springer Nature B.V
01.07.2001
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Persistent issues of corrosion degradation, both on the tubing inner diameter (ID) [primary water stress corrosion cracking (PWSCC)] and OD [intergranular attack (IGA) and stress corrosion cracking (SCC)] surfaces led to efforts to optimize the metallurgical characteristics of Alloy 600.1,2 The initial product of this research was a special thermal treatment, performed after final mill annealing to effect intergranular carbide precipitation; this product exhibited enhanced resistance to SCC and was designated... |
---|---|
Bibliography: | ObjectType-Article-2 SourceType-Scholarly Journals-1 ObjectType-Feature-1 content type line 23 |
ISSN: | 1047-4838 1543-1851 |
DOI: | 10.1007/s11837-001-0080-1 |