Application of Low Cost Polyurethane (PU) Foam for Fabricating Porous Tri-Calcium Phosphate (TCP)
Porous tri-calcium phosphate, well-known for its use as artificial bone, was prepared via sponge polymeric method by the application of low cost polyurethane (PU) foam as a structural guide. In this experiment, fractions of tri-calcium phosphate (TCP) are controlled at 12, 13, 14, 15 and 16 grams an...
Saved in:
Published in | Journal of biomimetics, biomaterials and biomedical engineering Vol. 8; pp. 1 - 7 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | English |
Published |
Zurich
Trans Tech Publications Ltd
01.11.2010
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Porous tri-calcium phosphate, well-known for its use as artificial bone, was prepared via sponge polymeric method by the application of low cost polyurethane (PU) foam as a structural guide. In this experiment, fractions of tri-calcium phosphate (TCP) are controlled at 12, 13, 14, 15 and 16 grams and mixed with distilled water (fixed at 25 grams) to produce slurries. Subsequently, rectangular shaped PU foam was immersed in the slurry and dried for three days. Samples were then sintered at 1100°C to obtain porous tri-calcium phosphate. This method produces porous tri-calcium phosphate with porosity between 31-44% and the compressive strength in the range of 0.17-1.02 MPa. The macroporosity of the tri-calcium phosphate, observed through SEM, was in the range of 100 µm to 900 µm. |
---|---|
ISSN: | 1662-1018 1662-100X 2296-9837 1662-100X 2296-9845 |
DOI: | 10.4028/www.scientific.net/JBBTE.8.1 |