An experimental approach for estimating the effect of heat affected zone (HAZ) microstructural gradient on fatigue crack growth rate in aluminum alloy FSW

The microstructural gradient of the heat affected zone (HAZ) in aluminum alloy FSW has been simulated experimentally by subjecting the parent alloy to a controlled aging process. The purpose of the simulation is to estimate the effect of the HAZ microstructural gradient on fatigue crack propagation...

Full description

Saved in:
Bibliographic Details
Published inMaterials science & engineering. A, Structural materials : properties, microstructure and processing Vol. 691; pp. 110 - 120
Main Authors Kermanidis, A.T., Tzamtzis, A.
Format Journal Article
LanguageEnglish
Published Lausanne Elsevier B.V 13.04.2017
Elsevier BV
Subjects
Aging (metallurgy)
Aluminum alloy
Aluminum alloys
Crack propagation
Fatigue crack growth
Fatigue failure
Fatigue tests
Fracture mechanics
Friction stir weld
Friction stir welding
Heat affected zone
Microhardness
Microstructural gradient
Microstructure
Residual stress
Simulation
Stress propagation
Welded joints
Fatigue crack growth
Friction stir weld
Heat affected zone
Microstructural gradient
Microhardness
Aluminum alloy
Online AccessGet full text

Cover

More Information
Summary:The microstructural gradient of the heat affected zone (HAZ) in aluminum alloy FSW has been simulated experimentally by subjecting the parent alloy to a controlled aging process. The purpose of the simulation is to estimate the effect of the HAZ microstructural gradient on fatigue crack propagation rate by excluding the effect of weld residual stresses. The microstructure in the gradient material produced by aging was evaluated against the actual FSW heat affected zone by comparing microstructural features and microhardness variation. Fatigue crack growth tests were conducted on the gradient material to evaluate its influence on crack propagation rate. The results showed that the gradient has a negative influence on fatigue crack propagation rate, accelerating crack growth with regard to the conditions at onset of the gradient. The impact on crack growth rate is dependent on the slope of the gradient with regard to the direction of fatigue crack propagation. The results of the study suggest that independent from the effect of weld residual stresses the micostructural influence in fatigue crack growth analysis of welded joints should not be neglected.
ISSN:0921-5093
1873-4936
DOI:10.1016/j.msea.2017.03.036