Investigation of magnetic order in a new intermetallic compound Nd2PtGe3
•A new compound Nd2PtGe3 was succesfully synthetized by an arc-melting method.•Nd2PtGe3 crystallizes in a disordered ternary variant of the AlB2-type structure.•Significant anisotropic broadening of X-ray diffraction peaks was observed.•Cluster glass behavior is seen below 3 K due to disorder and ma...
Saved in:
Published in | Journal of magnetism and magnetic materials Vol. 521; p. 167494 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Amsterdam
Elsevier B.V
01.03.2021
Elsevier BV |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | •A new compound Nd2PtGe3 was succesfully synthetized by an arc-melting method.•Nd2PtGe3 crystallizes in a disordered ternary variant of the AlB2-type structure.•Significant anisotropic broadening of X-ray diffraction peaks was observed.•Cluster glass behavior is seen below 3 K due to disorder and magnetic frustration.
In the present study we report a successful synthesis of the new intermetallic compound Nd2PtGe3 by an arc-melting method. The powder X-ray diffraction analysis indicates that this compound crystallizes in an disordered variant of the AlB2-type structure (space group P6/mmm, no. 191) with lattice parameters a = 4.2455 Å and c = 4. 1933 Å. The compound exhibits a cluster-glass transition below Tf = 2.9 K, characterized through ac and dc magnetic susceptibility and heat capacity measurements. |
---|---|