On the importance of local equilibria in alloy design criteria for bulk nano-pearlitic steels and ensuing mechanical properties

A critical review of the dependence of yield strength of pearlite on interlamellar spacing unveils the contribution of solid solution strengthening of ferrite. In order to understand the evolution of solute content within pearlitic ferrite, importance of various local equilibria modes (assumed to pe...

Full description

Saved in:
Bibliographic Details
Published inMaterials science & engineering. A, Structural materials : properties, microstructure and processing Vol. 841; p. 143034
Main Authors Tripathy, Snehashish, Sahu, Vikash Kumar, Jena, P.S. Manoranjan, Tarafder, Soumitro, Ghosh Chowdhury, Sandip
Format Journal Article
LanguageEnglish
Published Lausanne Elsevier B.V 28.04.2022
Elsevier BV
Subjects
Online AccessGet full text

Cover

Loading…
More Information
Summary:A critical review of the dependence of yield strength of pearlite on interlamellar spacing unveils the contribution of solid solution strengthening of ferrite. In order to understand the evolution of solute content within pearlitic ferrite, importance of various local equilibria modes (assumed to persist during transformation) has been realized and revisited in present work. With this understanding, an alloy composition and corresponding two stage cooling process have been designed to have nano-pearlitic microstructure (interlamellar spacing <100 nm). Characterization of elemental partitioning across the growing pearlite-austenite interface using scanning transmission electron microscopy coupled with energy dispersive x-ray spectroscopy (STEM-EDS) reveals no-partitioning growth mode of pearlite. Further, mechanical properties have been assessed for samples interrupted during cooling post pearlite formation (at 635 °C, S635) and for those cooled till room temperature (SRT). Reduction in ferrite width from ∼70 nm to ∼65 nm along with increase in post transformation enrichment of pearlitic ferrite with Si from S635 and SRT, has been shown to lead to an increase in the yield strength from ∼680 MPa to ∼775 MPa in the deigned alloy.