Investigation on micromechanism of ferrite hardening after pre-straining with different strain rates of dual-phase steel

• Published in: Materials science & engineering. A, Structural materials : properties, microstructure and processing Vol. 802; p. 140657
• Main Authors: Chen, Yongnan, Wu, Zhicheng, Wu, Gang, Wang, Nan, Zhao, Qinyang, Luo, Jinheng
• Format: Journal Article
• Language: English
• Published: Lausanne Elsevier B.V 20.01.2021; Elsevier BV
• Subjects: Bainite; Dual phase steels; Dual-phase steel; Elongation; Evolution; Ferrite; Ferrite hardening; Geometrically necessary dislocations; Grain boundaries; Kernel average misorientation; Localization; Misalignment; Nanohardness; Nanoindentation; Plastic deformation; Strain analysis; Strain localization; Strain rate; Structural steels; Tensile deformation; Tensile tests; Dual-phase steel; Ferrite hardening; Geometrically necessary dislocations; Strain rate; Kernel average misorientation
• ISSN: 0921-5093; 1873-4936
• DOI: 10.1016/j.msea.2020.140657

In this work, the effects of strain rates (10−4 s−1~10−1 s−1) on ferrite hardening of dual-phase steel were investigated through pre-straining tests. The strain localization was analyzed by the evolution of Kernel average misorientation (KAM). The micromechanism of ferrite hardening was elaborated by the evolution analysis of geometrically necessary dislocations (GNDs), low angle grain boundaries (LAGB) and nano-indentation. The results showed that GNDs and LAGBs in ferrite increased with increasing the strain rate, the average KAM values and nanohardness increased accordingly. Strain localization was observed in the ferrite grains at lower strain rates (10−4 s−1~10−3 s−1), and the considerable strain localization occurred at ferrite/bainite (F/B) interface at higher strain rates. Due to the nearly saturated GNDs and LAGBs density at the strain rate of 10−2 s−1, the completely ferrite hardening occurred and its nanohardness was close to dual-phase interface. During the tensile deformation after pre-straining, the yield ratio increased while the uniform elongation decreased with strain rates of pre-straining. It was worth noting that the completely ferrite hardening led to the early plastic deformation of tensile tests was interface deformation. This work provides a theoretical basis for the ferrite hardening behavior after pre-straining at different strain rates, and then contributes to the safe service of dual-phase pipeline steel. [Display omitted] •At the strain rate of 10−2 s−1, due to the nearly saturated GNDs and LAGBs density, the completely ferrite hardening occurs.•After pre-straining at higher strain rates, the completely ferrite hardening leads to the early stage of plastic deformation of tensile tests is interface deformation.