Enhanced broadband near-infrared emission and energy transfer in Bi-Tm-codoped germanate glasses for broadband optical amplification
Bi-Tm-codoped, and Tm- and Bi- singly doped germanate glasses were prepared, and their luminescent properties were investigated. Intense broadband near-IR emission with FWHM of 300 nm was observed in the Bi-Tm codoped glass. The emission intensity of Tm(3+):(3)H(4)-(13)F(4) and (3)F(4)-(13)H(5) tran...
Saved in:
Published in | Optics letters Vol. 34; no. 16; p. 2486 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | English |
Published |
United States
15.08.2009
|
Online Access | Get more information |
Cover
Loading…
Summary: | Bi-Tm-codoped, and Tm- and Bi- singly doped germanate glasses were prepared, and their luminescent properties were investigated. Intense broadband near-IR emission with FWHM of 300 nm was observed in the Bi-Tm codoped glass. The emission intensity of Tm(3+):(3)H(4)-(13)F(4) and (3)F(4)-(13)H(5) transitions in the Bi-Tm-codoped glass was highly increased and reduced, respectively. The fluorescence lifetime of Tm(3+) at 1470 nm increased from 204 micros to 301 micros after codoping. These should be due to the efficient energy transfer from Bi-related centers to Tm(3+) ions. The highest energy transfer efficiency is estimated to be approximately 50%. |
---|---|
ISSN: | 1539-4794 |
DOI: | 10.1364/OL.34.002486 |