p -type conduction from Sb-doped ZnO thin films grown by dual ion beam sputtering in the absence of oxygen ambient

• Published in: Journal of applied physics Vol. 114; no. 16
• Main Authors: Kumar Pandey, Sushil, Kumar Pandey, Saurabh, Awasthi, Vishnu, Kumar, Ashish, Deshpande, Uday P., Gupta, Mukul, Mukherjee, Shaibal
• Format: Journal Article
• Language: English
• Published: Melville American Institute of Physics 28.10.2013
• Subjects: ANNEALING; Antimony; Applied physics; CARRIER MOBILITY; Crystal structure; Current voltage characteristics; Deposition; Diffraction; DOPED MATERIALS; HETEROJUNCTIONS; Ion beam sputtering; ION BEAMS; MATERIALS SCIENCE; OXYGEN; SAPPHIRE; SEMICONDUCTOR MATERIALS; SPUTTERING; SUBSTRATES; SURFACES; TEMPERATURE RANGE 0273-0400 K; THIN FILMS; Volt-ampere characteristics; X ray spectra; X-RAY DIFFRACTION; X-RAY PHOTOELECTRON SPECTROSCOPY; X-rays; Zinc oxide; ZINC OXIDES
• ISSN: 0021-8979; 1089-7550
• DOI: 10.1063/1.4827379

Sb-doped ZnO (SZO) thin films were deposited on c-plane sapphire substrates by dual ion beam sputtering deposition system in the absence of oxygen ambient. The electrical, structural, morphological, and elemental properties of SZO thin films were studied for films grown at different substrate temperatures ranging from 200 °C to 600 °C and then annealed in situ at 800 °C under vacuum (pressure ∼5 × 10−8 mbar). Films grown for temperature range of 200–500 °C showed p-type conduction with hole concentration of 1.374 × 1016 to 5.538 × 1016 cm−3, resistivity of 66.733–12.758 Ω cm, and carrier mobility of 4.964–8.846 cm2 V−1 s−1 at room temperature. However, the film grown at 600 °C showed n-type behavior. Additionally, current-voltage (I–V) characteristic of p-ZnO/n-Si heterojunction showed a diode-like behavior, and that further confirmed the p-type conduction in ZnO by Sb doping. X-ray diffraction measurements showed that all SZO films had (002) preferred crystal orientation. X-ray photoelectron spectroscopy analysis confirmed the formation of SbZn–2VZn complex caused acceptor-like behavior in SZO films.