Preparation of a Novel Cationic Photosensitive Resin (3D-SLR01) for Stereolithography 3D Printing and Determination of Its Some Properties
A novel cationic photosensitive resin (3DSLR-01) for stereolithography 3D printing was prepared with 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate (2021P), 1,4-cyclohexanedimethanol glycidyl ether (JX-026), diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate (S-186), polycapro...
Saved in:
Published in | Journal of Wuhan University of Technology. Materials science edition Vol. 34; no. 4; pp. 761 - 768 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Wuhan
Wuhan University of Technology
01.08.2019
Springer Nature B.V |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | A novel cationic photosensitive resin (3DSLR-01) for stereolithography 3D printing was prepared with 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate (2021P), 1,4-cyclohexanedimethanol glycidyl ether (JX-026), diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate (S-186), polycaprolactone polyol(Polyol-0305), novolac epoxy resin(F-51), bis(3-ethyl-3-oxetanylmethyl) ether (S-221) and a mixture of triarylsulfonium hexafluoroantimonate salts solution (UVI-6976). The properties of the photosensitive resin and its UV-cured films were investigated by some instruments and equipment. The experimental results show that the critical exposure (
E
c
) of the photosensitive resin is 16.3 mJ/cm
2
, the penetration depth (
D
p
) is 0.14 mm, and the optical property of the photosensitive resin is excellent. Rectangle plates were printed by using a stereolithography apparatus (HRPL-150A) with the photosensitive resin as the manufacturing material, and the shrinkage rates of the plates were less than 0.60%, which showed that the accuracy of the manufactured plates was very high. |
---|---|