Improvement in a-plane GaN crystalline quality using wet etching method

Nonpolar （1120） GaN films are grown on the etched a-plane GaN substrates via metalorganic vapor phase epitaxy. High-resolution X-ray diffraction analysis shows great decreases in the full width at half maximum of the samples grown on etched substrates compared with those of the sample without etchin...

Full description

Saved in:
Bibliographic Details
Published inChinese physics B Vol. 23; no. 4; pp. 593 - 597
Main Author 曹荣涛 许晟瑞 张进成 赵一 薛军帅 哈微 张帅 崔培水 温慧娟 陈兴
Format Journal Article
LanguageEnglish
Published 01.04.2014
Subjects
Compressive properties
Crystal structure
Dislocation density
Etching
Etching (metallography)
Frequency ranges
Gallium nitrides
GaN薄膜
Stresses
X-射线衍射分析
位错密度
汽相外延
湿法蚀刻
结晶质量
薄膜生长
金属有机
Online AccessGet full text

Cover

More Information
Summary:Nonpolar （1120） GaN films are grown on the etched a-plane GaN substrates via metalorganic vapor phase epitaxy. High-resolution X-ray diffraction analysis shows great decreases in the full width at half maximum of the samples grown on etched substrates compared with those of the sample without etching, both on-axis and off-axis, indicating the reduced dislocation densities and improved crystalline quality of these samples. The spatial mapping of the E2 （high） phonon mode demonstrates the smaller line width with a black background in the wing region, which testifies the reduced dislocation densities and enhanced crystalline quality of the epitaxial lateral overgrowth areas. Raman scattering spectra of the E2 （high） peaks exhibit in-plane compressive stress for all the overgrowth samples, and the E2 （high） peaks of samples grown on etched substrates shift toward the lower frequency range, indicating the relaxations of in-plane stress in these GaN films. Furthermore, room temperature photoluminescence measurement demonstrates a significant decrease in the yellow-band emission intensity of a-plane GaN grown on etched templates, which also illustrates the better optical properties of these samples.
Bibliography:Nonpolar （1120） GaN films are grown on the etched a-plane GaN substrates via metalorganic vapor phase epitaxy. High-resolution X-ray diffraction analysis shows great decreases in the full width at half maximum of the samples grown on etched substrates compared with those of the sample without etching, both on-axis and off-axis, indicating the reduced dislocation densities and improved crystalline quality of these samples. The spatial mapping of the E2 （high） phonon mode demonstrates the smaller line width with a black background in the wing region, which testifies the reduced dislocation densities and enhanced crystalline quality of the epitaxial lateral overgrowth areas. Raman scattering spectra of the E2 （high） peaks exhibit in-plane compressive stress for all the overgrowth samples, and the E2 （high） peaks of samples grown on etched substrates shift toward the lower frequency range, indicating the relaxations of in-plane stress in these GaN films. Furthermore, room temperature photoluminescence measurement demonstrates a significant decrease in the yellow-band emission intensity of a-plane GaN grown on etched templates, which also illustrates the better optical properties of these samples.
11-5639/O4
nonpolar GaN, wet etching, metal-organic chemical vapor deposition, crystalline quality
ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
ISSN:1674-1056
2058-3834
1741-4199
DOI:10.1088/1674-1056/23/4/047804