Friction behavior of PTFE-coated Si3N4/TiC ceramics fabricated by spray technique under dry friction

• Published in: Ceramics international Vol. 47; no. 6; pp. 7487 - 7496
• Main Authors: Song, Wenlong, Wang, Shoujun, Lu, Yang, Zhang, Xuan, Xia, Zixiang
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 15.03.2021
• Subjects: Friction and wear behavior; PTFE coatings; Si3N4/TiC ceramics; Spraying; Friction and wear behavior; Si3N4/TiC ceramics; PTFE coatings; Spraying
• ISSN: 0272-8842; 1873-3956
• DOI: 10.1016/j.ceramint.2020.10.255

PTFE coatings were deposited on the Si3N4/TiC ceramic substrate by using spray technology. The surface and cross-section micrographs, adhesive force of coatings with substrate, surface roughness and micro-hardness of the coated ceramics were examined. The friction and wear behaviors of ceramic samples with and without coatings were investigated through carrying out dry sliding friction tests against WC/Co ball. The test results indicated that the coated ceramics exhibited rougher surface and lower micro-hardness, and the PTFE coatings can significantly reduce the surface friction and adhesive wear of ceramics. The friction performance of PTFE-coated sample was affected by applied load due to the lower surface hardness and shear strength of coatings, and the main wear failure mechanisms were abrasion wear, coating delamination and flaking. It can be considered that deposition of PTFE coatings is a promising approach to improve the friction and wear behavior of ceramic substrate.