Comparison of Friction Properties of GI Steel Plates with Various Surface Treatments

• Published in: Lubricants Vol. 12; no. 6; p. 198
• Main Authors: Tomáš, Miroslav, Németh, Stanislav, Evin, Emil, Hollý, František, Kundracik, Vladimír, Kulya, Juliy Martyn, Buber, Marek
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.06.2024
• Subjects: Coefficient of friction; Corrosion; Corrosion prevention; Corrosion resistance; Corrosion tests; cup test; Friction; friction coefficient; Galvanized steel; Hot dip galvanizing; Lubricants & lubrication; Mechanical properties; Metal forming; Metal sheets; Organic coatings; Passivity; Steel plates; Strain hardening; Substrates; Surface properties; Surface treatment; Tension tests; thin organic coating; Germany
• ISSN: 2075-4442; 2075-4442
• DOI: 10.3390/lubricants12060198

This article presents the improved properties of GI (hot-dip galvanized) steel plates in combination with a special permanent surface treatment. The substrate used was hot-dip galvanized deep-drawn steel sheets of grade DX56D + Z. Subsequently, various surface treatments were applied to their surface. The coefficient of friction of the metal sheets without surface treatment, with a temporary surface treatment called passivation, and a thin organic coating (TOC) based on hydroxyl resins dissolved in water, Ti and Cr3+ were determined by a cup test. The surface quality and corrosion resistance of all tested samples were also determined by exposing them for up to 288 h in an atmosphere of neutral salt spray. The surface microgeometry parameters Ra, RPc and Rz(I), which have a significant influence on the pressing process itself, were also determined. The TOC deposited on the Zn substrate was the only one to exhibit excellent lubrication and anticorrosion properties, resulting in the lowest surface microgeometry values owing to the uniform and continuous layer of the thin organic coating compared to the GI substrate and passivation surface treatment, respectively.