Effect of Exothermic Addition (CuO - Al) on the Structure, Mechanical Properties and Abrasive Wear Resistance of the Deposited Metal During Self-Shielded Flux-Cored Arc Welding
The microstructure evolution, mechanical properties, and tribological properties of deposited metal Fe-C-Cr-Ti-B alloy by self-shielded flux-cored wire electrode (FCAW S) with the introduction of exothermic addition and without it are investigated. Experimental studies showed that the introduction o...
Saved in:
Published in | Tribology in industry Vol. 43; no. 3; pp. 452 - 464 |
---|---|
Main Authors | , , , , , , , |
Format | Journal Article |
Language | English |
Published |
Kragujevac
University of Kragujevac, Faculty of Engineering
2021
University of Kragujevac |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The microstructure evolution, mechanical properties, and tribological properties of deposited metal Fe-C-Cr-Ti-B alloy by self-shielded flux-cored wire electrode (FCAW S) with the introduction of exothermic addition and without it are investigated. Experimental studies showed that the introduction of CuO Al exothermic addition in the composition of the wire core filler reduced the grain size of the deposited metal. Furthermore, X-ray diffraction analyses show that the boride layer contained FeB, Fe2B, and Ti(C, N) phases. Depth-sensing indentation was used to determine hard phase properties (hardness, Young's modulus and plasticity coefficient). It was shown that introduction of CuO –Al exothermic addition in the core filer increased the mechanical properties of deposited metal. The latter can be explained by the grain size decrease, as well as a change in the phase composition of the deposited metal due to additional copper alloying. This transformation is accompanied by an increase in hardness and in the Young's modulus. Tribological tests showed the effectiveness of introduction of the exothermic addition CuO –Al into the filler core for increasing the wear resistance under conditions of 3-body abrasive particle wear. |
---|---|