Study on the relationship between process organization and properties of 45MnVS non-tempered steel
The microstructure, mechanical properties, and heat treatment process relationships of 45MnVS non-tempered steel were investigated. Different grain sizes and tissue ratios were obtained after heating and holding at 950, 1050, and 1150 °C for 30 min, respectively, and cooling at different cooling con...
Saved in:
Published in | Matéria Vol. 29; no. 2 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English Portuguese |
Published |
Laboratório de Hidrogênio, Coppe - Universidade Federal do Rio de Janeiro; em cooperação com a Associação Brasileira do Hidrogênio, ABH2
2024
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The microstructure, mechanical properties, and heat treatment process relationships of 45MnVS non-tempered steel were investigated. Different grain sizes and tissue ratios were obtained after heating and holding at 950, 1050, and 1150 °C for 30 min, respectively, and cooling at different cooling conditions and cooling rates. As the austenitizing temperature increased, the grain size and the elongation and section shrinkage of the experimental steels decreased. At the same time, the content of ferrite and pearlite in the tissue gradually decreases, the content of sorbite and troostite rises, and the strength and hardness of the experimental steel increase. With the increase of cold speed, ferrite’s content decreases, sorbite and troostite’s content increases, and strength and hardness increase. The original austenite grain size also influences the tissue ratio. As the austenite grain refines, the ferrite transformation temperature increases during cooling and the ferrite content in the tissue rises after cooling. |
---|---|
ISSN: | 1517-7076 1517-7076 |
DOI: | 10.1590/1517-7076-rmat-2023-0316 |