Fatigue resistance of endodontic instruments manufactured in NiTi CM Wire and in conventional NiTi alloy with eletrochemical treatment

• Published in: RGO - Revista Gaúcha de Odontologia Vol. 66; no. 2; pp. 111 - 116
• Main Authors: INOJOSA, Inês de Fátima de Azevedo Jacinto, LOPES, Hélio Pereira, PEREIRA, Phillip Lucas Ricardo, NASCIMENTO, Diogo Lopes do, ELIAS, Carlos Nelson, VIEIRA, Victor Talarico Leal, VIEIRA, Marcia Valeria Boussada
• Format: Journal Article
• Language: English
• Published: Faculdade São Leopoldo Mandic 01.06.2018
• Subjects: Endodontics; Nickel; Titanium
• ISSN: 0103-6971; 1981-8637
• DOI: 10.1590/1981-863720180002000013308

ABSTRACT Objective: This study compared the fatigue behavior of endodontic instruments manufactured with conventional NiTi alloy electropolishing, RaCe (FKG Dentaire, LaChauxdeFonds, Switzerland), with instruments manufactured with NiTi CM Wire subjected to thermomechanical treatment, in the manufacturing process, HyFlex CM (Coltène Whaledent, Cuyahoga Falls, Ohio, USA), both with similar geometry and dimensions in order to determine the influence of the manufacturing process in the fatigue resistance. Methods: The methodoly consisted of twenty HyFlex CM and RaCe instruments with D0 0.25 mm, taper 0.06 mm / mm, 25 mm length, both with triangular cross section. The fracture resistance was evaluated by static fatigue test, using a stainless artificial canal with 5mm of radius (86°), recording the time and calculating the number of cycles until fracture occurs (NCF). For statistical analysis the Student t test was used The fractured instruments surface was analyzed by SEM. Results: The NCF was significantly higher for HyFlex CM instruments in comparison with RaCe files (P˂0.05) being 1336% more resistant to fatigue. The analysis of the fractured surface by SEM showed ductile-kind morphological characteristics for both instruments and the absence of plastic deformation. Conclusion: HyFlex CM instruments present higher values of NCF. Thus, it can be concluded that the thermal treatment to which these instruments with CM Wire alloy are submitted makes them more resistant to fracture than Race instruments manufactured with conventional NiTi alloy electropolishing. RESUMO Objetivo: Este estudo comparou a vida em fadiga de instrumentos endodônticos fabricados com a liga de NiTi convencional com eletropolimento de superfície, RaCe (FKG Dentaire, LaChauxdeFonds, Suiça), com instrumentos fabricados com a liga de NiTi CM Wire, submetidos a tratamento termomecânico, no processo de fabricação, HyFlex CM (Coltene Whaledent, Cuyahoga Falls, Ohio, EUA), ambos com geometria e dimensões semelhantes, visando determinar a influência do processo de fabricação das ligas e do acabamento superficial na resistência à fadiga. Métodos: Foram utilizados vinte instrumentos HyFlex CM e RaCe com D0 0,25mm, conicidade 0,06mm/mm, 25mm de comprimento, ambos com seção transversal triangular. A resistência à fratura foi avaliada através de teste estático de fadiga ciclica, utilizando um canal artificial em aço-inoxidável com 5mm de raio (86°), sendo registrado o tempo e calculado o número de ciclos para ocorrer a fratura (NCF). Para análise estatística empregou-se o teste t de Student. As superfícies de fratura dos instrumentos foram analisadas em MEV. Resultados: O NCF foi significativamente maior para os instrumentos HyFlex CM em comparação com as limas RaCe (p˂0,05), sendo 1336% mais resistentes à fadiga. A análise das superfícies fraturadas em MEV revelou características morfológicas do tipo dúctil para ambos os instrumentos e ausência de deformação plástica. Conclusão: Os instrumentos HyFlex CM apresentaram valores mais elevados de NCF. Deste modo, pode-se concluir que o tratamento térmico a qual estes instrumentos com a liga CM Wire foram submetidos os torna mais resistentes à fratura do que os instrumentos Race, fabricados com a liga de NiTi convencional com eletropolimento.