Synthesis and crystal chemistry of the new compounds GdBa4Cu3O8.5+δ and DyBa4Cu3O8.5+δ
Two new compounds, GdBa4Cu3O8.5+δ (Gd143) and DyBa4Cu3O8.5+δ (Dy143), were synthesized from precursors Gd2O3, Dy2O3, BaO2, and CuO at 1000 °C in an oxygen atmosphere. The oxygen stoichiometric value δ was found to be 0.68 for Gd143 and 0.6 for Dy143 by iodometric titration. Rietveld refinement of x-...
Saved in:
Published in | Journal of materials research Vol. 14; no. 2; pp. 334 - 339 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | English |
Published |
New York, USA
Cambridge University Press
01.02.1999
|
Online Access | Get full text |
Cover
Loading…
Summary: | Two new compounds, GdBa4Cu3O8.5+δ (Gd143) and DyBa4Cu3O8.5+δ (Dy143), were synthesized from precursors Gd2O3, Dy2O3, BaO2, and CuO at 1000 °C in an oxygen atmosphere. The oxygen stoichiometric value δ was found to be 0.68 for Gd143 and 0.6 for Dy143 by iodometric titration. Rietveld refinement of x-ray powder diffraction data showed that Gd143 belongs to the space group Pm3 while Dy143 belongs to the space group P23. The two space groups, Pm3 and P23, are very similar. Their main difference is that P23 does not have the inversion symmetry of Pm3. Both compounds have a cubic unit cell with a lattice parameter of 8.16528 ± 0.00006 Å for Gd143 and 8.10807 ± 0.00010 Å for Dy143. Superconducting quantum interference device (SQUID) measurement indicated that neither compound was superconductive down to 5 K. |
---|---|
Bibliography: | ArticleID:04750 istex:2376174EBEF85B08D4E5A56E6660514B19E5AFBF ark:/67375/6GQ-ZRC4WH3H-8 PII:S0884291400047506 ObjectType-Article-2 SourceType-Scholarly Journals-1 ObjectType-Feature-1 content type line 23 |
ISSN: | 0884-2914 2044-5326 |
DOI: | 10.1557/JMR.1999.0049 |