Morphological and thermal analyses of flexible polyurethane foams containing commercial calcium carbonate

• Published in: Eclética química Vol. 33; no. 2; pp. 55 - 60
• Main Authors: Sant'Anna, S. S., Souza, D. A., Carvalho, C. F., Yoshida, M. I.
• Format: Journal Article
• Language: English; Portuguese
• Published: Fundação Editora da Universidade Estadual Paulista Júlio de Mesquita Filho - UNESP 2008
• Subjects: CHEMISTRY, MULTIDISCIPLINARY; espuma flexível; carbonato de cálcio; polyurethane; flexible foam; calcium carbonate; poliuretano
• ISSN: 0100-4670; 1678-4618; 0100-4670
• DOI: 10.1590/S0100-46702008000200008

One filler often utilized in flexible polyurethane foams is calcium carbonate (CaCO3) because it is non-abrasiveness, non-toxicity and facilitated pigmentation. However, it is observed that the excess of commercial CaCO3 utilized in industry possibly causing permanent deformations and damaging the quality of the final product. The effect of different concentrations of commercial CaCO3, in flexible foams, was studied. Different concentrations of CaCO3 were used for the synthesis of flexible polyurethane foams, which were submitted to morphological and thermal analyses to verify the alterations provoked by the progressive introduction of this filler. Uma das cargas mais utilizadas na fabricação de espumas flexíveis de poliuretano é o carbonato de cálcio (CaCO3) por ser não abrasivo, não tóxico e de fácil pigmentação. Contudo, é observado que o excesso de CaCO3 comercial usado nas indústrias causa deformações permanentes, o que prejudica a qualidade do produto final. No presente trabalho é proposto o estudo do efeito da concentração de CaCO3 comercial na fabricação de espumas flexíveis de poliuretano. Foram utilizadas diferentes concentrações de CaCO3 na síntese das espumas, as quais foram submetidas à análises térmica e morfológica, afim de verificar as alterações provocadas pela introdução progressiva da carga.