Vesicular hydrogen silsesquioxane-mediated synthesis of nanocrystalline silicon dispersed in a mesoporous silica/suboxide matrix, with potential for electrochemical applications
Room temperature hydrolysis of triethoxysilane (TES) in the presence of pluronic P-123 (PEO 20 –PPO 70 –PEO 20 ) triblock copolymer under acidic conditions resulted in the formation of soft nanoscale vesicles with thin (<10 nm) hydrogen silsesquioxane (HSiO 1.5 ) n gel walls. FTIR and 29 Si MAS N...
Saved in:
Published in | New journal of chemistry Vol. 39; no. 1; pp. 621 - 630 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English |
Published |
United States
Royal Society of Chemistry
2015
|
Online Access | Get full text |
Cover
Loading…
Summary: | Room temperature hydrolysis of triethoxysilane (TES) in the presence of pluronic P-123 (PEO
20
–PPO
70
–PEO
20
) triblock copolymer under acidic conditions resulted in the formation of soft nanoscale vesicles with thin (<10 nm) hydrogen silsesquioxane (HSiO
1.5
)
n
gel walls. FTIR and
29
Si MAS NMR showed that pyrolysis of this material at 1000 °C in H
2
/Ar atmosphere led to decomposition of the hydrogen silsesquioxane with the resulting formation of a silicon suboxide surrounding Si nanocrystals, all embedded in a SiO
2
matrix. SEM, TEM, BET and SAXS measurements showed that this vesicular Si@SiO
x
–SiO
2
composite material had a high surface area and interconnected mesoporous structure. Nanocrystalline silicon was confirmed by XRD after the high temperature pyrolysis. An optimum in Li-ion battery half-cell performance was observed after the pyrolysis at 1000 °C, apparently attributable to the mesoporous structure and silicon nanocrystals. The effect of the polymer binders sodium carboxymethyl cellulose (CMC) and polyacrylic acid (PAA) on the cyclic performance was investigated by cyclic voltammetry and electrochemical impedance spectroscopy. Results suggest that the formation of the solid electrolyte interface layer is slower in the case of PAA, resulting in lower resistance to lithium diffusion at the interface. |
---|---|
Bibliography: | SC0001009 USDOE Advanced Research Projects Agency - Energy (ARPA-E) |
ISSN: | 1144-0546 1369-9261 |
DOI: | 10.1039/C4NJ01762E |