Influence of Sintering Temperature on the Thermoluminescence Spectra of MgSO4 Doped with RE(Tm,Dy) and Mn

• Published in: Applied Mechanics and Materials Vol. 664; no. Mechatronics and Mechanical Engineering I; pp. 57 - 61
• Main Authors: Tan, Zhi Jian, Guo, Jing Yuan, Zhang, Chun Xiang, Gao, Li, Luo, Da Ling, Lan, Ting Ting, Tang, Qiang
• Format: Journal Article
• Language: English
• Published: Zurich Trans Tech Publications Ltd 01.10.2014
• Subjects: Dysprosium; Ion emission; Phosphors; Rare earth metals; Sintering (powder metallurgy); Spectra; Spectral emissivity; Thermoluminescence; Thulium; TL; MgSO4; Dysprosium; Manganese
• ISBN: 9783038352921; 3038352926
• ISSN: 1660-9336; 1662-7482; 1662-7482
• DOI: 10.4028/www.scientific.net/AMM.664.57

In this paper, MgSO4:Dy,MgSO4:Tm and MgSO4:Mn phosphors are prepare by high temperature solid state reaction. The MgSO4:Dy or MgSO4:Tm powder are mixed and sintered with MgSO4:Mn respectively to obtain the co-doped MgSO4:Dy,Mn and MgSO4:Tm,Mn phosphors. The 3-dimensional thermoluminescence spectra of these two phosphors under different sintering temperature are measured.Results show that when the sintering temperature is below 800°C, Dy, Tm and Mn ions emissions are independent. However, when the sintering temperature was over 800°C, the emission peak of Mn becomes weaker, and so do the low temperature peaks of Dy and Tm, while the high temperature peaks of Dy and Tm become stronger. This indicated that the defect complex structure in the formation of the thermoluminescence material depends on the sintering temperature. As the sintering temperature rises, more and more Mn ions combine with the rare earth ions. Therefore, the luminescence process of the energy transfer of Mn ions to the rare earth ions can be observed and the suppression to low temperature peaks of Tm and Dy, and also shown in spectra.