Influence of Firing Regime and Potassium Ions on Synthetic Preparation of Belite Clinker
The study of the influence of selected temperature regime and potassium ions on the process of synthesis of belite (2CaO·SiO2, C2S) was carried out. The basic raw material was calcium carbonate (CaCO3) and amorphous silica (SiO2). The dosage of both components was based on the stoichiometric ratio o...
Saved in:
Published in | Binders, Materials and Technologies in Modern Construction V - 17th International Conference Silicate Binders (ICBM 2018) Vol. 296; p. 1 |
---|---|
Main Authors | , |
Format | Book Chapter Journal Article |
Language | English |
Published |
Zurich
Trans Tech Publications
16.08.2019
Trans Tech Publications Ltd |
Subjects | |
Online Access | Get full text |
ISBN | 3035715505 9783035715507 |
ISSN | 1012-0394 1662-9779 1662-9779 |
DOI | 10.4028/www.scientific.net/SSP.296.64 |
Cover
Loading…
Summary: | The study of the influence of selected temperature regime and potassium ions on the process of synthesis of belite (2CaO·SiO2, C2S) was carried out. The basic raw material was calcium carbonate (CaCO3) and amorphous silica (SiO2). The dosage of both components was based on the stoichiometric ratio of CaO:SiO2 in belite. The modification of the raw meal was carried out in the form of potash, K2O. Potash was dosed in the form of potassium carbonate, K2CO3, and potassium sulfate, K2SO4. The firing process was performed in a superkanthal furnace with two temperature modes, firing temperature: 1150 °C / 3 hours soaking and 1450 °C / 5 hours soaking. The evaluation performed by the experiment was based on mineralogical analysis by XRD analysis. |
---|---|
Bibliography: | Selected, peer reviewed papers from the 17th International Conference Silicate Binders (ICBM 2018), December 6, 2018, Brno, Czech Republic ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 14 |
ISBN: | 3035715505 9783035715507 |
ISSN: | 1012-0394 1662-9779 1662-9779 |
DOI: | 10.4028/www.scientific.net/SSP.296.64 |