Texturing behaviours of (K0.47Na0.51Li0.02)(Nb0.8Ta0.2)O3 piezoelectric ceramics produced using NaNb1-xTaxO3 templates

• Published in: Journal of the European Ceramic Society Vol. 38; no. 4; pp. 1442 - 1449
• Main Authors: Cha, Hyun Ae, Jeon, Jae-Ho
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 01.04.2018
• Subjects: (K0.47Na0.51Li0.02)(Nb0.8Ta0.2)O3; Lead-free piezoelectrics; Residual template; Texturing; (K0.47Na0.51Li0.02)(Nb0.8Ta0.2)O3; Lead-free piezoelectrics; Residual template; Texturing
• ISSN: 0955-2219; 1873-619X
• DOI: 10.1016/j.jeurceramsoc.2017.11.020

Textured (K0.47Na0.51Li0.02)(Nb0.8Ta0.2)O3 (KNLNT20) piezoelectric ceramics were prepared using NaNb1−xTaxO3 templates. The highest degree of grain orientation (97%) and piezoelectric constant (342 pC/N) were obtained upon adding 3wt% of the NaNb0.8Ta0.2O3 (NNT20) template and sintering at 1150°C for 1h. Back-scattered scanning electron micrographs of the textured KNLNT20 samples sintered at 1150°C for 1h indicated the presence of templates similar in size to the original ones within the cores of the textured grains. The peak value of the dielectric constant corresponding to the NNT20 core decreased after prolonged holding at 1150°C, owing to a decrease in the size of the NNT20 core because of the interdiffusion of K, Na, and Li ions between the NNT20 core and KNLNT20 shell. This interdiffusion also decreased the piezoelectric constant, d33 value of the textured KNLNT20 samples by inducing a change in the chemical composition of the shell region.