Phase formation with NaZn13 structure in metamagnetic La(Fe1–xCox)11.9Si1.1 compounds
The effects of different annealing conditions on the phase formation with NaZn13 structure were investigated in La(Fe1-xCox)11.9Si1.1 (x=0.068) compounds. It was found that the 1:13 phase was not formed directly from the melt upon cooling but via a peritectic reaction between the pro-peritectic gamm...
Saved in:
Published in | Journal of rare earths Vol. 26; no. 5; pp. 727 - 730 |
---|---|
Main Authors | , , , , , , |
Format | Journal Article |
Language | English |
Published |
School of Materials Science and Engineering,University of Science and Technology of Beijing,Beijing,100083,China
01.10.2008
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The effects of different annealing conditions on the phase formation with NaZn13 structure were investigated in La(Fe1-xCox)11.9Si1.1 (x=0.068) compounds. It was found that the 1:13 phase was not formed directly from the melt upon cooling but via a peritectic reaction between the pro-peritectic gamma-Fe and the La-rich phase. Annealing temperature was very important for the formation of 1:13 phase. Ice water was confirmed to be a preferable quenching medium. La(Fe1-xCox)11.9Si1.1 (x=0.068) compounds with almost single 1:13 phase were obtained at 1473 K after 15 d. |
---|---|
Bibliography: | ObjectType-Article-2 SourceType-Scholarly Journals-1 ObjectType-Feature-1 content type line 23 |
ISSN: | 1002-0721 2509-4963 |
DOI: | 10.1016/S1002-0721(08)60171-4 |