Dynamic Failure and Fragmentation of a Hot-Pressed Boron Carbide

• Published in: Journal of dynamic behavior of materials Vol. 3; no. 4; pp. 548 - 556
• Main Authors: Sano, Tomoko, Vargas-Gonzalez, Lionel, LaSalvia, Jerry, Hogan, James David
• Format: Journal Article
• Language: English
• Published: Cham Springer International Publishing 01.12.2017; Springer Nature B.V
• Subjects: Amorphization; Boron; Boron carbide; Chemistry and Materials Science; Experiments; Failure; Fragmentation; Materials Science; Mechanical properties; Metallic Materials; Penetration; Solid Mechanics; Transgranular fracture; Impact testing; Boron carbide; Failure; Fragmentation; Defects
• ISSN: 2199-7446; 2199-7454
• DOI: 10.1007/s40870-017-0133-3

This study investigates the failure and fragmentation of a hot-pressed boron carbide during high rate impact experiments. Four impact experiments are performed using a composite-backed target configuration at similar velocities, where two of the impact experiments resulted in complete target penetration and two resulted in partial penetration. This paper seeks to evaluate and understand the dynamic behavior of the ceramic that led to either the complete or partial penetration cases, focusing on: (1) surface and internal failure features of fragments using optical, scanning electron, and transmission electron microscopy, and (2) fragment size analysis using state-of-the-art particle-sizing technology that informs about the consequences of failure. Detailed characterization of the mechanical properties and the microstructure is also performed. Results indicate that transgranular fracture was the primary mode of failure in this boron carbide material, and no stress-induced amorphization features were observed. Analysis of the fragment sizes for the partial and completely penetrated experiments revealed a possible correlation between larger fragment sizes and impact performance. The results will add insight into designing improved advanced ceramics for impact protection applications.