Intrinsic Josephson junctions in Y1Ba2Cu3Ox single-crystal whiskers grown using Te-doped precursors
Single-crystal whiskers of Y1Ba2Cu3Ox with a length of about 5mm were grown from a Te-doped precursor. The optimum nominal composition of the precursors was Y2Ba3Cu3Te0.5Ox. From the energy-dispersive x-ray spectroscopy measurement, Te was not detected in the whiskers. The current-voltage (I-V) char...
Saved in:
Published in | Journal of applied physics Vol. 98; no. 7 |
---|---|
Main Authors | , , , , , , , , , |
Format | Journal Article |
Language | English |
Published |
01.10.2005
|
Online Access | Get full text |
Cover
Loading…
Summary: | Single-crystal whiskers of Y1Ba2Cu3Ox with a length of about 5mm were grown from a Te-doped precursor. The optimum nominal composition of the precursors was Y2Ba3Cu3Te0.5Ox. From the energy-dispersive x-ray spectroscopy measurement, Te was not detected in the whiskers. The current-voltage (I-V) characteristics along the c axis of an annealed in vacuum whisker exhibit a clear multibranched structure and a hysteresis curve corresponding to intrinsic Josephson junctions. |
---|---|
ISSN: | 0021-8979 1089-7550 |
DOI: | 10.1063/1.2064312 |