Studying the erosion corrosion behavior of NICrALY coating layer applied on AISI 446 stainless steel using thermal spray technique
Erosion-Corrosion behavior of NiCrAlY coatings deposited on 446 stainless steel samples by flame thermal spraying was performed in this research. The hardnessof uncoated and coated sample ismeasured, usingHVS-1000 Digital Micro hardness Tester. The results of hardness show that the coated samples ha...
Saved in:
Published in | Engineering and Technology Journal Vol. 38; no. 11A; pp. 1676 - 1683 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | English |
Published |
Baghdad, Iraq
University of Technology
25.11.2020
Unviversity of Technology- Iraq |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Erosion-Corrosion behavior of NiCrAlY coatings deposited on 446 stainless steel samples by flame thermal spraying was performed in this research. The hardnessof uncoated and coated sample ismeasured, usingHVS-1000 Digital Micro hardness Tester. The results of hardness show that the coated samples have higher hardness than uncoated samples. Microstructure and phase analysis of the coating layer was observed by using optical microscope, X-ray diffraction (XRD), and SEM respectively. Erosion –Corrosion testwas performed in different period of time (6, 12, and 18 hr. ) using the erosion-corrosion system. The result shows that because of uniform distributionandhomogeneous of coating layer, weight loss was very low and approximately equal in all period of testing time |
---|---|
ISSN: | 1681-6900 2412-0758 |
DOI: | 10.30684/etj.v38i11A.1691 |