Effect of Mn Contents on the Phase Transition of the High Entropy Alloy Prepared by Laser Cladding
Al1.3FeCoNiCuCr high entropy alloy (HEA) coatings were prepared by pre-placed laser cladding on 921A steel substrate, and the study on the phase transition of the Al1.3FeCoNiCuCr coating due to the introduction of Mn was conducted. The combination of TEM and XRD results showed that the Al1.3FeCoNiCu...
Saved in:
Published in | Materials science forum Vol. 849; pp. 64 - 70 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Pfaffikon
Trans Tech Publications Ltd
01.03.2016
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Al1.3FeCoNiCuCr high entropy alloy (HEA) coatings were prepared by pre-placed laser cladding on 921A steel substrate, and the study on the phase transition of the Al1.3FeCoNiCuCr coating due to the introduction of Mn was conducted. The combination of TEM and XRD results showed that the Al1.3FeCoNiCuCr HEA coatings without Mn addition typically consisted of two kinds of grains, i.e., one is composed of only FCC phase, and the another is a mixture of BCC and FCC phases. The two phases were of similar ratio in the coatings, while nanoparticulate precipitates were observed in the bcc phase. When 3 wt. % Mn was introduced into the alloy, the coatings consisted of also FCC and BCC phase. However, most of the grains were in FCC phase, while the BCC phase with a lath shape only distributed between the FCC phases. High hardness nanobanded precipitates were observed in the FCC phase. It is clearly revealed that the phase structure of Al1.3FeCoNiCuCr coatings undergoes a dramatic transition due to the introducing of Mn. |
---|---|
Bibliography: | Selected, peer reviewed papers from the Chinese Materials Conference 2015, July 10-14, 2015, Guiyang, China |
ISSN: | 0255-5476 1662-9752 1662-9752 |
DOI: | 10.4028/www.scientific.net/MSF.849.64 |