Investigation of the Interaction of Y2O3–Al2O3–SiO2 Coatings with Water Vapor and Na2SO4 at Temperatures to 1450°C
Coatings based on the system Y 2 O 3 –Al 2 O 3 –SiO 2 are promising for protecting silicon carbide based materials from the effects of an oxidizing atmosphere, water vapor, and salt vapors. The interaction of Y 2 O 3 –Al 2 O 3 –SiO 2 coatings, obtained by the sol-gel method, with water vapor and Na...
Saved in:
Published in | Glass and ceramics Vol. 78; no. 7-8; pp. 301 - 307 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English |
Published |
New York
Springer US
01.11.2021
Springer Nature B.V |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Coatings based on the system Y
2
O
3
–Al
2
O
3
–SiO
2
are promising for protecting silicon carbide based materials from the effects of an oxidizing atmosphere, water vapor, and salt vapors. The interaction of Y
2
O
3
–Al
2
O
3
–SiO
2
coatings, obtained by the sol-gel method, with water vapor and Na
2
SO
4
salt was investigated. Coatings based on the yttrium aluminosilicate system were found to have good oxidative and chemical resistance to water vapor and Na
2
SO
4
salt at temperatures 1300 – 1450°C. The weight gain for the coated samples tested in Na
2
SO
4
salt vapor did not exceed 1%. The initial SiC substrates are characterized by active oxidation processes with weight reduction from 8 to 11%. |
---|---|