The effect of the extrusion route (A, C and BC) on grain refinement during ECAP process in 99.9995% (5N5) high pure aluminum using a die with a channel-intersection angle 90° was investigated. It was found through experiment that, the grain was very coarse in the cast ingot of 5N5 high pure aluminum...
Saved in:
Published in | Advanced materials research Vol. 790; pp. 90 - 93 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Trans Tech Publications Ltd
04.09.2013
|
Subjects | |
Online Access | Get more information |
Cover
Loading…
Summary: | The effect of the extrusion route (A, C and BC) on grain refinement during ECAP process in 99.9995% (5N5) high pure aluminum using a die with a channel-intersection angle 90° was investigated. It was found through experiment that, the grain was very coarse in the cast ingot of 5N5 high pure aluminum, and the average grain size is about 50~60mm. After two ECAP passes, the average grain size is 300μm, 550μm and 200μm respectively with the extrusion route of Route A, C and BC. After eight ECAP passes, the average grain size is 100μm, 100μm and 30μm respectively with the extrusion route of Route A, C and BC. It indicates that the route BC is more effective than Route A and C. TEM micrograph of 5N5 high pure Al with different ECAP pass under Route BC was studied. |
---|---|
Bibliography: | Selected, peer reviewed papers from the 2013 International Conference on Advanced Engineering Materials and Architecture Science (ICAEMAS 2013), July 27-28, 2013, Xi’an, Shaanxi, China |
ISSN: | 1022-6680 1662-8985 1662-8985 |
DOI: | 10.4028/www.scientific.net/AMR.790.90 |