Sm-doped manganese-based Zr-Fe polymeric pillared interlayered montmorillonite for low temperature selective catalytic reduction of NO x by NH 3 in metallurgical sintering flue gas

• Published in: RSC advances Vol. 8; no. 73; pp. 42017 - 42024
• Main Authors: Han, Zhicheng, Yu, Qingbo, Xue, Zhijia, Liu, Kaijie, Qin, Qin
• Format: Journal Article
• Language: English
• Published: England 18.12.2018
• ISSN: 2046-2069; 2046-2069
• DOI: 10.1039/c8ra09434a

In this work, Sm-doped manganese supported Zr-Fe polymeric pillared interlayered montmorillonites (Mn/ZrFe-PILMs) were prepared for the low-temperature selective catalytic reduction (SCR) of NO with NH in metallurgical sintering flue gas. These pillared interlayered montmorillonite catalysts were characterized by X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy, nitrogen adsorption-desorption isotherm, ammonia temperature-programmed desorption, and hydrogen temperature-programmed reduction to study the influence of Sm doping on the SCR performance. The ZrFe-PILMs with a Mn/Sm molar ratio of 18 : 2 showed the excellent SCR activity among these catalysts, where a 95.5% NO conversion ratio at 200 °C at a space velocity of 20 000 h was obtained. Samarium oxide and manganese oxides were highly dispersed on the ZrFe-PILMs with different Mn/Sm molar ratios by the XRD results and SEM-EDS results. Meanwhile, the Mn-Sm/ZrFe-PILM (18 : 2) had the lowest temperature hydrogen reduction peak by H -TPR results, which indicated that it had the lowest active bond energy on its surface. And the NH -TPD results expressed that the Mn-Sm/ZrFe-PILM (18 : 2) had the most acidic sites, especially the weakly acidic sites. Therefore, it was found that the introduction of a small amount of Sm (Mn : Sm = 18 : 2) to Mn/ZrFe-PILM can significantly improve catalytic activity by the increased active oxygen component and the surface acidity.