Chemical Composition Modulation Realizing Remarkable Improvement of Thermoelectric Performance in CuInTe2‑Based Alloy

• Published in: ACS applied materials & interfaces Vol. 16; no. 18; pp. 23596 - 23605
• Main Authors: Qu, Luping, Luo, Yong, Li, Cong, Du, Zhengliang, Li, Xie, Cui, Jiaolin
• Format: Journal Article
• Language: English
• Published: American Chemical Society 23.04.2024
• Subjects: Functional Inorganic Materials and Devices; lattice thermal conductivity (κL); CuInTe2; thermoelectrics; chemical composition modulation; copper deficiency (VCu); carrier and phonon transport
• ISSN: 1944-8244; 1944-8252
• DOI: 10.1021/acsami.4c02739

CuInTe2 (CIT) is one of the typical ternary chalcogenides known for its characteristic mixed polyanionic/polycationic site defects, making it a subject of continuous interest in the field of thermoelectrics. In this work, we propose a chemical composition modulation strategy for CIT by alloying GeTe and then introducing a copper deficiency (denoted by VCu). This strategy aims to unpin its Fermi level (F r) and shift F r into the valence band (VB) while simultaneously enabling coupling between the optical and acoustic phonon, thereby providing an extra phonon scattering path at low frequencies. The simultaneous composition regulations not only enhance the carrier concentration (n H) to 1019–1020 cm–3 but also significantly reduce the lattice thermal conductivity (κL) to ∼0.48 W m–1 K–1, thus effectively realizing electro-acoustic coordination in the present material. As a consequence, the thermoelectric (TE) performance is remarkably improved with the highest TE figure of merit (ZT) of 1.51 at ∼838 K. This value ranks at a higher level among CIT-based materials, which showcases the great significance of chemical composition modulation.