PROCESS FOR PRODUCING GRAIN-ORIENTED MAGNETIC STEEL SHEET, GRAIN-ORIENTED MAGNETIC STEEL SHEET FOR WOUND CORE, AND WOUND CORE
A slab having a given composition is heated to 1,280ºC or higher. The slab is hot-rolled to obtain a hot-rolled steel sheet. The hot-rolled steel sheet is annealed to obtain an annealed steel sheet. The annealed steel sheet is cold-rolled to obtain a cold-rolled steel sheet. The cold-rolled steel sh...
Saved in:
Main Authors | , , , , , , |
---|---|
Format | Patent |
Language | English French Japanese |
Published |
30.09.2010
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Abstract | A slab having a given composition is heated to 1,280ºC or higher. The slab is hot-rolled to obtain a hot-rolled steel sheet. The hot-rolled steel sheet is annealed to obtain an annealed steel sheet. The annealed steel sheet is cold-rolled to obtain a cold-rolled steel sheet. The cold-rolled steel sheet is subjected to decarburization annealing to obtain a decarburized/annealed steel sheet. The decarburized/annealed steel sheet is wound into a coil. The decarburized/annealed steel sheet coil is finish-annealed. When the temperature of the cold-rolled steel sheet is elevated during or before the decarburization annealing, the cold-rolled steel sheet is heated to a temperature of 800ºC or higher at a rate of 30-100 ºC/sec. When the decarburized/annealed steel sheet is heated in the finish annealing, the decarburized/annealed steel sheet is heated at a rate of 20 ºC/h or lower in the temperature range of 750-1,150ºC.
Selon l'invention, une brame présentant une composition donnée est chauffée à 1 280 °C ou plus. La brame est laminée à chaud pour obtenir une tôle d'acier laminée à chaud. La tôle d'acier laminée à chaud est soumise à un recuit pour obtenir une tôle d'acier recuite. La tôle d'acier recuite est laminée à froid pour obtenir une tôle d'acier laminée à froid. La tôle d'acier laminée à froid est soumise à un recuit de décarburation pour obtenir une feuille d'acier décarburée/recuite. La tôle d'acier décarburée/recuite est enroulée en bobine. La bobine de tôle d'acier décarburée/recuite est soumise à un recuit. Lorsque la température de la tôle d'acier laminée à froid est élevée, pendant ou avant le recuit de décarburation, la tôle d'acier laminée à froid est chauffée à une température de 800 °C ou plus à raison de 30 à 100°C/s. Lorsque la tôle d'acier décarburée/recuite est chauffée dans le recuit de finition, la tôle d'acier décarburée/recuite est chauffée à raison de 20 °C/h ou moins, dans la plage de température de 750 à 1 150°C. |
---|---|
AbstractList | A slab having a given composition is heated to 1,280ºC or higher. The slab is hot-rolled to obtain a hot-rolled steel sheet. The hot-rolled steel sheet is annealed to obtain an annealed steel sheet. The annealed steel sheet is cold-rolled to obtain a cold-rolled steel sheet. The cold-rolled steel sheet is subjected to decarburization annealing to obtain a decarburized/annealed steel sheet. The decarburized/annealed steel sheet is wound into a coil. The decarburized/annealed steel sheet coil is finish-annealed. When the temperature of the cold-rolled steel sheet is elevated during or before the decarburization annealing, the cold-rolled steel sheet is heated to a temperature of 800ºC or higher at a rate of 30-100 ºC/sec. When the decarburized/annealed steel sheet is heated in the finish annealing, the decarburized/annealed steel sheet is heated at a rate of 20 ºC/h or lower in the temperature range of 750-1,150ºC.
Selon l'invention, une brame présentant une composition donnée est chauffée à 1 280 °C ou plus. La brame est laminée à chaud pour obtenir une tôle d'acier laminée à chaud. La tôle d'acier laminée à chaud est soumise à un recuit pour obtenir une tôle d'acier recuite. La tôle d'acier recuite est laminée à froid pour obtenir une tôle d'acier laminée à froid. La tôle d'acier laminée à froid est soumise à un recuit de décarburation pour obtenir une feuille d'acier décarburée/recuite. La tôle d'acier décarburée/recuite est enroulée en bobine. La bobine de tôle d'acier décarburée/recuite est soumise à un recuit. Lorsque la température de la tôle d'acier laminée à froid est élevée, pendant ou avant le recuit de décarburation, la tôle d'acier laminée à froid est chauffée à une température de 800 °C ou plus à raison de 30 à 100°C/s. Lorsque la tôle d'acier décarburée/recuite est chauffée dans le recuit de finition, la tôle d'acier décarburée/recuite est chauffée à raison de 20 °C/h ou moins, dans la plage de température de 750 à 1 150°C. |
Author | TAKEBAYASHI, SEIKI MORISHIGE, NOBUSATO HONMA, HOTAKA TANAKA, KOKI MURAKAMI, KENICHI MIZUKAMI, KAZUMI KUBO, YUJI |
Author_xml | – fullname: HONMA, HOTAKA – fullname: TANAKA, KOKI – fullname: KUBO, YUJI – fullname: MIZUKAMI, KAZUMI – fullname: TAKEBAYASHI, SEIKI – fullname: MORISHIGE, NOBUSATO – fullname: MURAKAMI, KENICHI |
BookMark | eNrjYmDJy89L5WSoDQjyd3YNDlZw8w9SALJdQp09_dwV3IMcPf10_YM8Xf1CXF0UfB3d_VxDPJ0VgkNcXX0Ugj1cXUN0iFEENjbcP9TPRcHZP8hVR8ERyELweRhY0xJzilN5oTQ3g7Kba4izh25qQX58anFBYnJqXmpJfLi_kYGhgaGhgZGhuaOhMXGqAAvEPYs |
ContentType | Patent |
DBID | EVB |
DatabaseName | esp@cenet |
DatabaseTitleList | |
Database_xml | – sequence: 1 dbid: EVB name: esp@cenet url: http://worldwide.espacenet.com/singleLineSearch?locale=en_EP sourceTypes: Open Access Repository |
DeliveryMethod | fulltext_linktorsrc |
Discipline | Medicine Chemistry Sciences |
DocumentTitleAlternate | PROCÉDÉ DE PRODUCTION D'UNE FEUILLE D'ACIER MAGNÉTIQUE À GRAINS ORIENTÉS, FEUILLE D'ACIER MAGNÉTIQUE À GRAINS ORIENTÉS POUR NOYAU ENROULÉ, ET NOYAU ENROULÉ |
ExternalDocumentID | WO2010110217A1 |
GroupedDBID | EVB |
ID | FETCH-epo_espacenet_WO2010110217A13 |
IEDL.DBID | EVB |
IngestDate | Fri Jul 19 14:50:37 EDT 2024 |
IsOpenAccess | true |
IsPeerReviewed | false |
IsScholarly | false |
Language | English French Japanese |
LinkModel | DirectLink |
MergedId | FETCHMERGED-epo_espacenet_WO2010110217A13 |
Notes | Application Number: WO2010JP54846 |
OpenAccessLink | https://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20100930&DB=EPODOC&CC=WO&NR=2010110217A1 |
ParticipantIDs | epo_espacenet_WO2010110217A1 |
PublicationCentury | 2000 |
PublicationDate | 20100930 |
PublicationDateYYYYMMDD | 2010-09-30 |
PublicationDate_xml | – month: 09 year: 2010 text: 20100930 day: 30 |
PublicationDecade | 2010 |
PublicationYear | 2010 |
RelatedCompanies | TAKEBAYASHI, SEIKI MORISHIGE, NOBUSATO HONMA, HOTAKA NIPPON STEEL CORPORATION TANAKA, KOKI MURAKAMI, KENICHI MIZUKAMI, KAZUMI KUBO, YUJI |
RelatedCompanies_xml | – name: MIZUKAMI, KAZUMI – name: TAKEBAYASHI, SEIKI – name: MURAKAMI, KENICHI – name: KUBO, YUJI – name: TANAKA, KOKI – name: MORISHIGE, NOBUSATO – name: NIPPON STEEL CORPORATION – name: HONMA, HOTAKA |
Score | 2.8918734 |
Snippet | A slab having a given composition is heated to 1,280ºC or higher. The slab is hot-rolled to obtain a hot-rolled steel sheet. The hot-rolled steel sheet is... |
SourceID | epo |
SourceType | Open Access Repository |
SubjectTerms | ALLOYS BASIC ELECTRIC ELEMENTS CHEMISTRY ELECTRICITY FERROUS OR NON-FERROUS ALLOYS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS INDUCTANCES MAGNETS MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS PERFORMING OPERATIONS PUNCHING METAL ROLLING OF METAL SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES TRANSFORMERS TRANSPORTING TREATMENT OF ALLOYS OR NON-FERROUS METALS |
Title | PROCESS FOR PRODUCING GRAIN-ORIENTED MAGNETIC STEEL SHEET, GRAIN-ORIENTED MAGNETIC STEEL SHEET FOR WOUND CORE, AND WOUND CORE |
URI | https://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20100930&DB=EPODOC&locale=&CC=WO&NR=2010110217A1 |
hasFullText | 1 |
inHoldings | 1 |
isFullTextHit | |
isPrint | |
link | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwjV3dT8IwEG8IGvVNUeMHmiaaPbEIbAP2QMzoCsxIS8YQ3ki3bonGAJEZn_zfvdUhPBHfrh-55C653v161ytC9zWzaRgylrqM64ZuJlWhh4kR6cKSUVKXth2pJq4D1uiPzaepNS2g9_VbGNUn9Es1RwSLisDeU3VeLzeXWK6qrVw9hK8wtXjsBm1Xy9FxLQPoVc3ttOmQu5xohABu05iv1mrZN9ZNB7DSHgTSzawAjL50sncpy22n0j1G-0PgN09PUOFNlNAhWf-9VkIHgzzlDWRufatT9D30OQGFYUBuGGh3TDzWwz3f8ZjOfY8yOIbwwOkxGngEjwJKn_GoT2lQ-c8mxXbCx8zFhPu0gh2gNuMzdNelAenrIMfsT22zCd8W2jhHxfliHl8gHEZSCjtpSRlapmi1BMSEUoS2lfUiatTtS1Texelq9_I1OvrNsGc1FWVUTD8-4xtw3Gl4q_T9AxnIkm4 |
link.rule.ids | 230,309,783,888,25578,76884 |
linkProvider | European Patent Office |
linkToHtml | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwjV3dT8IwEG8IGvFNUeMHahPNnlgEtsH2QMzoCpuyjowhvJFt3RKNASIzPvm_e6sgPBHfrh-5pJfcXX9t71eE7utqS1F4wmWeNBRZTWuhHKVKLIcaj9MGN4xYkLi6rGmP1KeJNimg93UtjOAJ_RLkiOBRMfh7JuL1YnOIZYm3lcuH6BW65o_doG1JK3RczwF6TbI6bTrwLI9IhABuk5gvxur5N9YtE7DSHmyy9Zxpn7508rqUxXZS6R6h_QHom2XHqPAWllGJrP9eK6MDd3XlDeLK-5Yn6HvgewQMhgG5YZCtEXFYD_d802Gy5zuUQRjCrtljNHAIHgaU9vHQpjSo_meSUDv2RszCxPNpFZsgbdqn6K5LA2LLsI7pn9mmY2970coZKs7ms-Qc4SjmPDRSnfNIU0NdD2FPyMPI0HIuombDuECVXZoudw_fopIduP1p32HPV-jw97Y9f19RQcXs4zO5hiSeRTfC9j8hW5Ve |
openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Apatent&rft.title=PROCESS+FOR+PRODUCING+GRAIN-ORIENTED+MAGNETIC+STEEL+SHEET%2C+GRAIN-ORIENTED+MAGNETIC+STEEL+SHEET+FOR+WOUND+CORE%2C+AND+WOUND+CORE&rft.inventor=HONMA%2C+HOTAKA&rft.inventor=TANAKA%2C+KOKI&rft.inventor=KUBO%2C+YUJI&rft.inventor=MIZUKAMI%2C+KAZUMI&rft.inventor=TAKEBAYASHI%2C+SEIKI&rft.inventor=MORISHIGE%2C+NOBUSATO&rft.inventor=MURAKAMI%2C+KENICHI&rft.date=2010-09-30&rft.externalDBID=A1&rft.externalDocID=WO2010110217A1 |