STEEL SHEET FOR CANS AND MANUFACTURING METHOD THEREOF

• Main Authors: NAKAMARU, HIROKI, TADA, MASAKI, STEIN-FECHNER, KATHLEEN, KOJIMA, KATSUMI, TANAKA, TAKUMI, KAUP, BURKHARD, NAKAGAWA, YUSUKE
• Format: Patent
• Language: English; French
• Published: 21.05.2019
• Subjects: ALLOYS; CHEMISTRY; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; TREATMENT OF ALLOYS OR NON-FERROUS METALS

This steel sheet for cans contains, in mass%, C: 0.0030% or less, Si: 0.02% or less, Mn: 0.05%-0.60%, P: 0.020% or less, S: 0.020% or less, Al: 0.010%-0.100%, N: 0.0010%-0.0050% and Nb: 0.001%-0.050%, the remainder being Fe and unavoidable impurities. It holds that (integrated intensity of (111)[1-21] orientation)/(integrated intensity of (111)[1-10] orientation) ? 0.9, and in the rolling direction and the direction 90° from the rolling direction in the horizontal plane, it holds that the tensile strength TS ? 550 and the elongation at break E1 > -0.02×TS+17.5. L'invention concerne une feuille d'acier pour boîtes métalliques, contenant en pourcentage en masse de : 0,0030 % de C ou inférieur, 0,02 % de Si ou inférieur, 0,05 à 0,60 % de Mn, 0,020 % de P ou inférieur, 0,020 % de S ou inférieur, 0,010 % à 0,100 % d'Al, 0,0010 % à 0,0050 % de N et 0,001 % à 0,050 % de Nb, le reste étant constitué de Fe et d'impuretés inévitables. La feuille d'acier selon l'invention respecte les conditions suivantes: (intensité intégrée d'orientation (111)[1 -21])/(intensité intégrée d'orientation (111)[1-10]) = 0,9 ; et, dans la direction de laminage et la direction à 90° de la direction de laminage sur le plan horizontal, la résistance à la traction est TS = 550 et l'allongement à la rupture est E1 > -0,02×TS+17,5.