고인성 탄소/에폭시 복합재료의 제조 및 특성 분석
Interlaminar delamination is an important problem in applications of carbon fiber reinforced composites. Delamination occurs due to the presence of matrix cracks, causes fiber breakage, and results in the loss of stiffness and strength, which may lead to safety and reliability problems. In this stud...
Saved in:
Published in | 한국섬유공학회지 Vol. 54; no. 1; pp. 54 - 59 |
---|---|
Main Authors | , , , , , , , , , |
Format | Journal Article |
Language | Korean |
Published |
한국섬유공학회
28.02.2017
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Interlaminar delamination is an important problem in applications of carbon fiber reinforced composites. Delamination occurs due to the presence of matrix cracks, causes fiber breakage, and results in the loss of stiffness and strength, which may lead to safety and reliability problems. In this study, the effect of polyethersulfone (PES) of the epoxy resin on interlaminar shear strength and fracture toughness of carbon/epoxy composites was investigated. Consequently, interlaminar bonding increased with proper addition of PES, but excess PES led to loss of interlaminar bonding of the carbon/epoxy composite. |
---|---|
Bibliography: | The Korean Fiber Society KISTI1.1003/JNL.JAKO201711656579646 G704-000008.2017.54.1.002 |
ISSN: | 1225-1089 2288-6419 |