Synthesis of Iron Oxide Yellow from Spent Pickling Solutions
This paper demonstrates a simple environment-friendly synthesis route of iron oxide yellow (α-FeOOH) using spent pickling solutions as raw material. After abundant laboratory experiments, we finally pinned down the best procedure. The research showed that α-FeOOH nanometer material with average diam...
Saved in:
| Published in | MATEC Web of Conferences Vol. 67; p. 6091 |
|---|---|
| Main Authors | , , , |
| Format | Journal Article Conference Proceeding |
| Language | English |
| Published |
Les Ulis
EDP Sciences
01.01.2016
|
| Subjects | |
| Online Access | Get full text |
Cover
Loading…
| Abstract | This paper demonstrates a simple environment-friendly synthesis route of iron oxide yellow (α-FeOOH) using spent pickling solutions as raw material. After abundant laboratory experiments, we finally pinned down the best procedure. The research showed that α-FeOOH nanometer material with average diameter of 50nm and average length of 400 nm was prepared at the optimal technique. And the FeOOH content of the sample was as high as 90%, which is higher than the 86% of GB/T1863-2008. The structure, morphology and size distribution of the product was characterized by X-ray diffraction (XRD), Transmission electron microscope (TEM), Scanning electron microscope (SEM) and Malvern lazer particle analyzer, respectively. The test results show that all the indices of as-prepared iron oxide yellow are completely in conformity with and even better than national primes standard. |
|---|---|
| AbstractList | This paper demonstrates a simple environment-friendly synthesis route of iron oxide yellow (α-FeOOH) using spent pickling solutions as raw material. After abundant laboratory experiments, we finally pinned down the best procedure. The research showed that α-FeOOH nanometer material with average diameter of 50nm and average length of 400 nm was prepared at the optimal technique. And the FeOOH content of the sample was as high as 90%, which is higher than the 86% of GB/T1863-2008. The structure, morphology and size distribution of the product was characterized by X-ray diffraction (XRD), Transmission electron microscope (TEM), Scanning electron microscope (SEM) and Malvern lazer particle analyzer, respectively. The test results show that all the indices of as-prepared iron oxide yellow are completely in conformity with and even better than national primes standard. |
| Author | Wan, Guangqin Lv, Feifei Yang, Yaqiang Wang, Xingyao |
| Author_xml | – sequence: 1 givenname: Guangqin surname: Wan fullname: Wan, Guangqin – sequence: 2 givenname: Feifei surname: Lv fullname: Lv, Feifei – sequence: 3 givenname: Yaqiang surname: Yang fullname: Yang, Yaqiang – sequence: 4 givenname: Xingyao surname: Wang fullname: Wang, Xingyao |
| BookMark | eNpNUF1LAzEQDFLBWvsThAOfaze5XD7AFyl-FAoVqqBPIZdL6tVrUpMr2n_vaaX0ZXcZZmeGOUc9H7xF6BLDNYYCj9e6tcYE78YEMGMcGEh8gvqEMDwiOXvtHd1naJjSCgBwLjlI3kc3i51v322qUxZcNo3BZ_PvurLZm22a8JW5GNbZYmN9mz3V5qOp_TJbhGbb1sGnC3TqdJPs8H8P0Mv93fPkcTSbP0wnt7ORySVtO-dSkkIwDBbnJZGGl4IRS7v4nGkClJpcm8JYApxy5qgjvBsSCuEYrlw-QNO9bhX0Sm1ivdZxp4Ku1R8Q4lLp2NamsUp3P45KbSxImgshjKYl1oIUuBIFg07raq-1ieFza1OrVmEbfRdfESg4kRIL0rGKPcvEkFK07uCKQf32rg69q6Pe8x9ea3fs |
| CitedBy_id | crossref_primary_10_1007_s11270_022_05835_y |
| Cites_doi | 10.1016/j.hydromet.2010.01.003 10.1016/j.resconrec.2011.11.010 10.1016/j.powtec.2013.04.034 10.1016/j.matlet.2013.04.004 10.1016/j.materresbull.2006.04.030 10.1016/j.matlet.2005.12.053 10.1080/00986440500192238 10.1016/S0304-386X(96)00066-7 10.1063/1.4849273 10.1016/j.psep.2010.11.005 10.1016/j.jallcom.2005.09.043 10.1021/ja01107a510 10.1016/j.matlet.2004.10.066 10.1149/1.2424416 10.1016/j.ceramint.2014.06.051 10.1021/jp909072m 10.1016/j.hydromet.2006.03.058 10.1007/s11051-008-9467-z 10.1016/0921-3449(94)90047-7 10.1016/j.jece.2013.05.007 10.1016/S0167-577X(01)00546-8 |
| ContentType | Journal Article Conference Proceeding |
| Copyright | 2016. This work is licensed under http://creativecommons.org/licenses/by/4.0/ (the “License”). Notwithstanding the ProQuest Terms and conditions, you may use this content in accordance with the terms of the License. |
| Copyright_xml | – notice: 2016. This work is licensed under http://creativecommons.org/licenses/by/4.0/ (the “License”). Notwithstanding the ProQuest Terms and conditions, you may use this content in accordance with the terms of the License. |
| DBID | AAYXX CITATION 7SP 7SR 7TB 8BQ 8FD 8FE 8FG ABJCF ABUWG AFKRA AZQEC BENPR BGLVJ CCPQU D1I DWQXO FR3 HCIFZ JG9 KB. KR7 L6V L7M M7S PDBOC PIMPY PQEST PQQKQ PQUKI PRINS PTHSS DOA |
| DOI | 10.1051/matecconf/20166706091 |
| DatabaseName | CrossRef Electronics & Communications Abstracts Engineered Materials Abstracts Mechanical & Transportation Engineering Abstracts METADEX Technology Research Database ProQuest SciTech Collection ProQuest Technology Collection Materials Science & Engineering Collection ProQuest Central (Alumni) ProQuest Central UK/Ireland ProQuest Central Essentials AUTh Library subscriptions: ProQuest Central Technology Collection ProQuest One Community College ProQuest Materials Science Collection ProQuest Central Engineering Research Database SciTech Premium Collection (Proquest) (PQ_SDU_P3) Materials Research Database https://resources.nclive.org/materials Civil Engineering Abstracts ProQuest Engineering Collection Advanced Technologies Database with Aerospace ProQuest Engineering Database Materials Science Collection ProQuest Publicly Available Content database ProQuest One Academic Eastern Edition (DO NOT USE) ProQuest One Academic ProQuest One Academic UKI Edition ProQuest Central China Engineering Collection Open Access: DOAJ - Directory of Open Access Journals |
| DatabaseTitle | CrossRef Publicly Available Content Database Materials Research Database Technology Collection Technology Research Database Mechanical & Transportation Engineering Abstracts ProQuest Central Essentials Materials Science Collection ProQuest Central (Alumni Edition) SciTech Premium Collection ProQuest One Community College ProQuest Central China ProQuest Central Engineered Materials Abstracts ProQuest Engineering Collection ProQuest Central Korea Materials Science Database Advanced Technologies Database with Aerospace Engineering Collection ProQuest Materials Science Collection Civil Engineering Abstracts Engineering Database ProQuest One Academic Eastern Edition Electronics & Communications Abstracts ProQuest Technology Collection ProQuest SciTech Collection METADEX ProQuest One Academic UKI Edition Materials Science & Engineering Collection Engineering Research Database ProQuest One Academic |
| DatabaseTitleList | Publicly Available Content Database |
| Database_xml | – sequence: 1 dbid: DOA name: DOAJ Directory of Open Access Journals url: https://www.doaj.org/ sourceTypes: Open Website – sequence: 2 dbid: 8FG name: ProQuest Technology Collection url: https://search.proquest.com/technologycollection1 sourceTypes: Aggregation Database |
| DeliveryMethod | fulltext_linktorsrc |
| Discipline | Engineering |
| EISSN | 2261-236X |
| Editor | Kenawy, El-R. Jawaid, M. |
| Editor_xml | – sequence: 1 givenname: M. surname: Jawaid fullname: Jawaid, M. – sequence: 2 givenname: El-R. surname: Kenawy fullname: Kenawy, El-R. |
| ExternalDocumentID | oai_doaj_org_article_a58ff49ace0943888ca4b1a8251d8560 10_1051_matecconf_20166706091 |
| Genre | Conference Proceeding |
| GroupedDBID | 4.4 5VS 8FE 8FG AAFWJ AAYXX ABJCF ACACO ACIWK ADBBV AFKRA AFPKN ALMA_UNASSIGNED_HOLDINGS ARCSS BCNDV BENPR BGLVJ CCPQU CITATION D1I EBS EJD GI~ GROUPED_DOAJ HCIFZ IPNFZ KB. KQ8 L6V M7S M~E OK1 PDBOC PIMPY PROAC PTHSS RED RIG RNS 7SP 7SR 7TB 8BQ 8FD ABUWG AZQEC DWQXO FR3 JG9 KR7 L7M PQEST PQQKQ PQUKI PRINS |
| ID | FETCH-LOGICAL-c394t-23b9258610e13b29c7b862e405176a2044c3ac5ce207476f4f27f4f9058f61df3 |
| IEDL.DBID | 8FG |
| ISSN | 2261-236X 2274-7214 |
| IngestDate | Tue Oct 22 14:53:53 EDT 2024 Thu Oct 10 18:14:16 EDT 2024 Fri Aug 23 01:52:52 EDT 2024 |
| IsDoiOpenAccess | true |
| IsOpenAccess | true |
| IsPeerReviewed | true |
| IsScholarly | true |
| Language | English |
| LinkModel | DirectLink |
| MergedId | FETCHMERGED-LOGICAL-c394t-23b9258610e13b29c7b862e405176a2044c3ac5ce207476f4f27f4f9058f61df3 |
| OpenAccessLink | https://www.proquest.com/docview/2057299182?pq-origsite=%requestingapplication% |
| PQID | 2057299182 |
| PQPubID | 2040549 |
| ParticipantIDs | doaj_primary_oai_doaj_org_article_a58ff49ace0943888ca4b1a8251d8560 proquest_journals_2057299182 crossref_primary_10_1051_matecconf_20166706091 |
| PublicationCentury | 2000 |
| PublicationDate | 2016-01-01 |
| PublicationDateYYYYMMDD | 2016-01-01 |
| PublicationDate_xml | – month: 01 year: 2016 text: 2016-01-01 day: 01 |
| PublicationDecade | 2010 |
| PublicationPlace | Les Ulis |
| PublicationPlace_xml | – name: Les Ulis |
| PublicationTitle | MATEC Web of Conferences |
| PublicationYear | 2016 |
| Publisher | EDP Sciences |
| Publisher_xml | – name: EDP Sciences |
| References | Schiemann (R4) 2013; 245 Bashir (R15) 2009; 11 Kraus (R10) 1953; 75 Ristic (R14) 2006; 417 Jozsef (R7) 1976; 969 Kirci (R6) 2013; 1569 Villalba (R13) 2013; 104 Darroudi (R9) 2014; 40 Krehula (R17) 2002; 54 Duraesa (R19) 2005; 59 Geng (R16) 2006; 41 Rogener (R12) 2012; 60 Ciminelli (R2) 2006; 84 Martinez (R20) 2007; 154 Langova (R11) 2010; 101 Jaiswal (R18) 2013; 1 Jiao (R21) 2010; 114 Kerney (R8) 1994; 10 Ozdemir (R3) 2006; 193 Zhang (R22) 2006; 60 Lopez-Delgoda (R1) 1997; 45 Ferreira (R5) 2011; 89 |
| References_xml | – volume: 101 start-page: 171 year: 2010 ident: R11 publication-title: Hydrometallurgy doi: 10.1016/j.hydromet.2010.01.003 contributor: fullname: Langova – volume: 969 start-page: 207 year: 1976 ident: R7 publication-title: U.S. patent 3 contributor: fullname: Jozsef – volume: 60 start-page: 72 year: 2012 ident: R12 publication-title: Conservation and Recycling doi: 10.1016/j.resconrec.2011.11.010 contributor: fullname: Rogener – volume: 245 start-page: 70 year: 2013 ident: R4 publication-title: Powder Technol. doi: 10.1016/j.powtec.2013.04.034 contributor: fullname: Schiemann – volume: 104 start-page: 17 year: 2013 ident: R13 publication-title: Mater. Lett. doi: 10.1016/j.matlet.2013.04.004 contributor: fullname: Villalba – volume: 41 start-page: 2238 year: 2006 ident: R16 publication-title: Mater. Res. Bull. doi: 10.1016/j.materresbull.2006.04.030 contributor: fullname: Geng – volume: 60 start-page: 1915 year: 2006 ident: R22 publication-title: Mater. Lett. doi: 10.1016/j.matlet.2005.12.053 contributor: fullname: Zhang – volume: 193 start-page: 548 year: 2006 ident: R3 publication-title: Chem. Eng. Commun. doi: 10.1080/00986440500192238 contributor: fullname: Ozdemir – volume: 45 start-page: 97 year: 1997 ident: R1 publication-title: Hydrometallurgy doi: 10.1016/S0304-386X(96)00066-7 contributor: fullname: Lopez-Delgoda – volume: 1569 start-page: 265 year: 2013 ident: R6 publication-title: AIP Conf. Proc. doi: 10.1063/1.4849273 contributor: fullname: Kirci – volume: 89 start-page: 172 year: 2011 ident: R5 publication-title: Process Saf. Environ. Prot. doi: 10.1016/j.psep.2010.11.005 contributor: fullname: Ferreira – volume: 417 start-page: 292 year: 2006 ident: R14 publication-title: J. Alloys Compd. doi: 10.1016/j.jallcom.2005.09.043 contributor: fullname: Ristic – volume: 75 start-page: 2768 year: 1953 ident: R10 publication-title: J. Am. Chem. Soc. doi: 10.1021/ja01107a510 contributor: fullname: Kraus – volume: 59 start-page: 859 year: 2005 ident: R19 publication-title: Mater. Lett. doi: 10.1016/j.matlet.2004.10.066 contributor: fullname: Duraesa – volume: 154 start-page: 126 year: 2007 ident: R20 publication-title: J. Electrochem. Soc. doi: 10.1149/1.2424416 contributor: fullname: Martinez – volume: 40 start-page: 14641 year: 2014 ident: R9 publication-title: Ceramics International doi: 10.1016/j.ceramint.2014.06.051 contributor: fullname: Darroudi – volume: 114 start-page: 269 year: 2010 ident: R21 publication-title: J. Phys. Chem. C doi: 10.1021/jp909072m contributor: fullname: Jiao – volume: 84 start-page: 37 year: 2006 ident: R2 publication-title: Hydrometallurgy doi: 10.1016/j.hydromet.2006.03.058 contributor: fullname: Ciminelli – volume: 11 start-page: 701 year: 2009 ident: R15 publication-title: J. Nanopart Res. doi: 10.1007/s11051-008-9467-z contributor: fullname: Bashir – volume: 10 start-page: 145 year: 1994 ident: R8 publication-title: Res. Conserv. Recycl. doi: 10.1016/0921-3449(94)90047-7 contributor: fullname: Kerney – volume: 1 start-page: 281 year: 2013 ident: R18 publication-title: J. Environ. Chem. Eng. doi: 10.1016/j.jece.2013.05.007 contributor: fullname: Jaiswal – volume: 54 start-page: 108 year: 2002 ident: R17 publication-title: Mater. Lett. doi: 10.1016/S0167-577X(01)00546-8 contributor: fullname: Krehula |
| SSID | ssj0001397097 |
| Score | 2.016292 |
| Snippet | This paper demonstrates a simple environment-friendly synthesis route of iron oxide yellow (α-FeOOH) using spent pickling solutions as raw material. After... |
| SourceID | doaj proquest crossref |
| SourceType | Open Website Aggregation Database |
| StartPage | 6091 |
| SubjectTerms | Electron microscopes Iron oxides Morphology Particle size distribution Pickling Synthesis X-ray diffraction |
| SummonAdditionalLinks | – databaseName: Open Access: DOAJ - Directory of Open Access Journals dbid: DOA link: http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwrV09T8MwELVQJxgQn6JQkAfWUDv-SCyxAKIqDIBUKpUpsh0blSGp2iLg33NO0iqIgYUlQxTJp3eO753te4fQOUR0KjVVUawtJChM28g4TSJiBNcQ0RKmK7XPBzkc8_uJmLRafYU7YbU8cA1cX4vUe660deEOHORrVnNDdai4zFMI19XqS1QrmXpreA1RyapkR9A-8D-wtiw8pPtUyiAao-iPYFRp9v9akqs4M9hB2w1BxFe1YbtowxV7aKslG7iPLkdfBfC2xXSBS4_v5mWBHz-nucMv4STlA4eSETyaQTjBT1MbWrK_4vX21wEaD26fb4ZR0wUhskzxZRQzo2KRAs1xlJlY2cRAFuJ4ENeSOiacW0BYWBcHLXzpuY8TeCgCwEmae3aIOkVZuCOEdSpSRnKROwNEgiZGp04k3luT5sDDXBddrODIZrXYRVYdUguarfHLWvh10XUAbf1x0KquXoAHs8aD2V8e7KLeCvKs-YEWMIgA2q8g-zn-jzFO0GYwu9476aHOcv7uToFNLM1ZNXG-AV2TxcU priority: 102 providerName: Directory of Open Access Journals |
| Title | Synthesis of Iron Oxide Yellow from Spent Pickling Solutions |
| URI | https://www.proquest.com/docview/2057299182 https://doaj.org/article/a58ff49ace0943888ca4b1a8251d8560 |
| Volume | 67 |
| hasFullText | 1 |
| inHoldings | 1 |
| isFullTextHit | |
| isPrint | |
| link | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwfV07T8MwELagLDDxKKI8Kg-sgdix85CQkEBtKQNUlEowRbZjV12S0hQBC7-ds5u0RUgsHpIosk62v-_Od98hdA6ITkJBEo8KBQ5KIJQntfA9X3ImANGiQDi1z4fwbsTuX_hLFXArq7TK-kx0B3VWKBsjByedAw9MgA5fT9882zXK3q5WLTQ20RahUWSdr7jbW8VYAGx911-FUpt2SAmri3g4uQRGCPMvcgP_JmFoZWQS8guenIr_n0PaIU93FzVXNXl4sESbPbSh8320syYneICuhl858LlyUuLC4P6syPHj5yTT-NXesHxgW0qCh1OAGTyYKNuqfYyXYbEmGnU7z7d3XtUdwVNBwuYeDWRCeQz0R5NA0kRFErwTzazoViioz5gCy3OlqdXIDw0zNIIh8XlsQpKZ4BA18iLXRwiLmMeBn_FMSyAYJJIi1jwyRsk4A36mW-iiNko6XYhgpO7ympN0acV0zYotdGNNt_zYali7B8VsnFZbIhUwEcMSobTNbgRPXAkmibC1tFkMRKyFTmvDp9XGKtPVMjj-__UJ2rYTWkRLTlFjPnvXZ8Af5rLtFkkbbd10HgZPbeeFw9jrf_8AS3TFeA |
| link.rule.ids | 310,311,315,783,787,792,793,867,2109,12777,21400,23942,23943,25152,27936,27937,33385,33756,43612,43817 |
| linkProvider | ProQuest |
| linkToHtml | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwfV3JTsMwELVYDsCJVRQK-MA1EDt2FgkJCURpoSxSqVROlu3YqJektEXA3zNOk7QIiUsOiRVZI9vvzXjmDUKngOgklCTxqNTgoARSe8pI3_MVZxIQLQpkofb5GLb77G7AB2XAbVKmVVZnYnFQp7l2MXJw0jnwwATo8OXo3XNdo9ztatlCYxmtsgCw2lWKt27nMRYAW7_or0KpSzukhFVFPJycAyOE-eeZhX-TMHQyMgn5BU-Fiv-fQ7pAntYm2p3X5OHnGm220JLJttHGgpzgDrrofWfA5ybDCc4t7ozzDD99DVODX90Nyyd2pSS4NwKYwc9D7Vq1v-E6LLaL-q2bl-u2V3ZH8HSQsKlHA5VQHgP9MSRQNNGRAu_EMCe6FUrqM6bB8lwb6jTyQ8ssjeCR-Dy2IUltsIdWsjwz-wjLmMeBn_LUKCAYJFIyNjyyVqs4BX5mGuisMooYzUQwRHF5zYmorSgWrNhAV8509WCnYV28yMdvotwSQsJELEukNi67ETxxLZki0tXSpjEQsQZqVoYX5caaiPkyOPj_8wlaa788dEW383h_iNbd5GaRkyZamY4_zBFwiak6LhbMDyplxJw |
| openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Ajournal&rft.genre=proceeding&rft.title=MATEC+Web+of+Conferences&rft.atitle=Synthesis+of+Iron+Oxide+Yellow+from+Spent+Pickling+Solutions&rft.au=Wan%2C+Guangqin&rft.au=Lv%2C+Feifei&rft.au=Yang%2C+Yaqiang&rft.au=Wang%2C+Xingyao&rft.date=2016-01-01&rft.pub=EDP+Sciences&rft.issn=2274-7214&rft.eissn=2261-236X&rft.volume=67&rft_id=info:doi/10.1051%2Fmatecconf%2F20166706091 |
| thumbnail_l | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/lc.gif&issn=2261-236X&client=summon |
| thumbnail_m | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/mc.gif&issn=2261-236X&client=summon |
| thumbnail_s | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/sc.gif&issn=2261-236X&client=summon |