A study of induced delamination and failure in woven composite laminates subject to short-beam shear testing - Espadas-Escalante, J.J.; Isaksson, P. (Engineering fracture mechanics, 2019)
Keywords: Computed tomography; Damage; Delamination; Failure mechanisms; Finite element analysis; Finite element method; Interface fracture; Laminates; Scanning electron microscopy; Stress concentration; Stress distribution; Woven composites; X-ray computed tomography; Finite element analysis; X-ray computed tomography; Damage; Interface fracture; Woven composites