Effects of inclusion types on the high-cycle fatigue properties of high-strength steel

• Published in: Scripta materialia Vol. 206; p. 114232
• Main Authors: Wang, P., Wang, B., Liu, Y., Zhang, P., Luan, Y.K., Li, D.Z., Zhang, Z.F.
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 01.01.2022
• Subjects: Fatigue cracking; High carbon chromium bearing steel; High-cycle fatigue; Inclusion types; Stress intensity factor; Inclusion types; Stress intensity factor; High-cycle fatigue; Fatigue cracking; High carbon chromium bearing steel

The high-cycle fatigue fracture behavior induced by different types of inclusions for high-strength steels was investigated. It is found that fatigue cracking of high carbon chromium bearing steel mainly originated from the interface between the matrix and the oxide inclusions while from the inside...