Severe tempering of bainite generated at low transformation temperatures
The response of a strong bainitic-steel to tempering at high temperatures is investigated, because a softened state is sometimes necessary during the manufacture of engineering components, prior to the final heat-treatment which hardens the material. Thermodynamic calculations conducted to determine...
Saved in:
Published in | International journal of materials research Vol. 103; no. 11; pp. 1319 - 1324 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | English |
Published |
Munich
De Gruyter
01.11.2012
Hanser |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The response of a strong bainitic-steel to tempering at high temperatures is investigated, because a softened state is sometimes necessary during the manufacture of engineering components, prior to the final heat-treatment which hardens the material. Thermodynamic calculations conducted to determine the maximum temperature at which the steel could be annealed without forming austenite were found to significantly overestimate the actual temperature at which austenite, ferrite and cementite (γ + α + θ) can coexist in equilibrium. As a consequence, the tempering temperature must be limited to below about 700°C, which unfortunately necessitates many days of tempering in order to reduce the hardness to < 250 HV. An alloy modification which may shorten this tempering time is suggested. One unexpected outcome is that the unintended heat treatment in the three-phase field revealed useful information about the nucleation of pearlite on cementite particles. Colonies of pearlite started inevitably on particles of cementite located at the γ / α interfaces, rather than at similar particles enclosed completely by the austenite. |
---|---|
Bibliography: | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
ISSN: | 1862-5282 2195-8556 |
DOI: | 10.3139/146.110788 |