Damage and fracture of a ceramic matrix composite under isothermal and thermomechanical fatigue loading

• Published in: Theoretical and applied fracture mechanics Vol. 95; pp. 218 - 232
• Main Author: Longbiao, Li
• Format: Journal Article
• Language: English
• Published: Amsterdam Elsevier Ltd 01.06.2018; Elsevier BV
• Subjects: Ceramic fibers; Ceramic matrix composites; Ceramic-matrix composites (CMCs); Crack propagation; Cyclic loads; Cyclic testing; Damage; Debonding; Fatigue failure; Fatigue tests; Fiber composites; Fracture; Fractures; Hysteresis loops; Interfacial shear stresses; Material properties; Shear stress; Sliding; Thermomechanical fatigue; Thermomechanical fatigue; Ceramic-matrix composites (CMCs); Fracture; Damage

•The damage and fracture of long-fiber-reinforced ceramic-matrix composites (CMCs) under isothermal cyclic fatigue, dwell-fatigue and thermomechanical fatigue have been investigated.•The relationships between the cyclic temperature, cycle number, stress level, matrix multicracking, interface debondi...