Sliding wear behavior of a ferritic–pearlitic ductile cast iron with different nodule count - Abedi, H.R.; Fareghi, A.; Saghafian, H.; Kheirandish, S.H. (Wear, 2010)
Keywords: Applied sciences; Cast iron; Electron microscopy; Exact sciences and technology; Fatigue; Fracture mechanics (crack, fatigue, damage...); Friction, wear, lubrication; Fundamental areas of phenomenology (including applications); Machine components; Mechanical engineering. Machine design; Physics; Sliding wear; Solid mechanics; Structural and continuum mechanics; Three-body abrasion; Fatigue; Three-body abrasion; Sliding wear; Electron microscopy; Cast iron; Heat treatment; Adhesive wear; Wear test; Experimental study; Cast metal; Dry friction; Lapping; Wear rate; Oxidative degradation; Graphite; Wear resistance; ASTM standard; Microstructure; Delamination; Pin disk test; Ductile cast iron; Sliding friction; Tribology