Combustion synthesis of TiAl intermetallics and their simultaneous joining to carbon/carbon composites

• Published in: Scripta materialia Vol. 65; no. 3; pp. 261 - 264
• Main Authors: Cao, J., Wang, H.Q., Qi, J.L., Lin, X.C., Feng, J.C.
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 01.08.2011
• Subjects: Aluminides; Carbon; Carbon/carbon composites; Combustion synthesis; Intermetallic compounds; Intermetallics; Joining; Microstructure; Titanium aluminides; Titanium base alloys; Titanium compounds; Combustion synthesis; Titanium aluminides; Joining; Microstructure; Carbon/carbon composites
• ISSN: 1359-6462; 1872-8456
• DOI: 10.1016/j.scriptamat.2011.04.021

► The fabrication and simultaneous joining of TiAl intermetallics to C/C composites was realized using combustion synthesis. ► The interfacial compressive stresses were obtained using the specific configuration with a C/C ball into Ti-Al mixtures. ► TiAl and Ti 3Al phases were identified in the reaction products of Ti-Al powder mixtures. ► The interfacial microstructure consisted of TiC and TiAl 3 layers from C/C composites to TiAl intermetallics. The combustion synthesis of TiAl intermetallics and their joining to carbon/carbon composites was realized simultaneously. The successful joint configuration involved putting a carbon/carbon composite ball into the Ti–Al powder mixtures. The effect of the residual stresses at the interface on the joining of carbon/carbon composite to TiAl intermetallics was analyzed. Investigation of the reaction products of Ti–45 at.% Al mixtures showed that TiAl and Ti 3Al phases were formed by combustion synthesis. The evolution of the interfacial microstructure was investigated.