High-temperature corrosion mechanism of YSZ coatings subject to calcium–magnesium–aluminosilicate (CMAS) deposits: First-principles calculations - Zheng, Haizhong; Chen, Zheng; Li, Guifa; Shu, Xiaoyong; Peng, Ping (Corrosion science, 2017)
Keywords: Aluminum silicates; Calcium; Calcium aluminate; CMAS; Coatings; Corrosion; Corrosion mechanisms; Delamination mechanism; Diffusion; First-principle calculation; High temperature; Magnesium; Mathematical analysis; Phase transitions; YSZ thermal barrier coatings; Yttria-stabilized zirconia; Yttrium oxide; Zirconium dioxide; First-principle calculation; YSZ thermal barrier coatings; CMAS; Delamination mechanism