Dual-scale porosity effects on crack growth in additively manufactured metals: 3D ductile fracture models - Muro-Barrios, R.; Cui, Y.; Lambros, J.; Chew, H.B. (Journal of the mechanics and physics of solids, 2022)
Keywords: Additive manufacturing; Additively manufactured metals; Crack growth; Crack propagation; Crack tips; Defects; Dual-scale voids; Ductile fracture; Failure; Finite element method; Fracture toughness; Metals; Porosity; Porous materials; Three dimensional boundary layer; Three dimensional models; Titanium base alloys; Tortuosity; Void growth and coalescence; Finite element method; Void growth and coalescence; Dual-scale voids; Additively manufactured metals; Crack growth; Fracture toughness