Effect of Ball Scribing on Power Loss Separation of Fe-3%Si Grain-oriented Silicon Steel
Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and rati...
Saved in:
Published in | Journal of Wuhan University of Technology. Materials science edition Vol. 31; no. 2; pp. 435 - 439 |
---|---|
Main Authors | , , , , , , |
Format | Journal Article |
Language | English |
Published |
Wuhan
Wuhan University of Technology
01.04.2016
Springer Nature B.V |
Subjects | |
Online Access | Get full text |
Cover
Loading…
Abstract | Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss. |
---|---|
AbstractList | Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss. Power loss of Fe-3%Si grain-oriented silicon steel was measured after ball scribing with different spacing using a self-designed tool. Three different sections of power loss, including hysteresis loss, abnormal loss, and eddy current loss, were measured and calculated, respectively. The loss variation and ratio were analyzed based on the experimental data. At 1.0 T, hysteresis loss of tested steel with scribing spacing of 8 mm descends by 8.2% compared to samples without scribing, which is similar to the total loss variation, and abnormal loss descends by 16.8%. At 1.0 T, hysteresis loss ratio of the steel with scribing spacing of 16 mm ascends from 55.7% to 57.9%, and eddy current loss increases from 17.4% to 24.1%, while abnormal loss descends from 26.9% to 23.7%. The experimental results show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormal loss. |
Author | WANG Hao LI Changsheng ZHAN Jianbo YU Zhenhua JI Yafeng WANG Guanglei PERIN Deni |
AuthorAffiliation | Materials Research Institute, Technical Center of China Tobacco Yunnan Industrial Co., Ltd., Kunming 650231, China State KeyLaboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China Engineering Research Center for Departmentof Heavy Machinery Education, Taiyuan University of Science and Technology, Taiyuan 030024, China Nanjing Iron and Steel Co. Ltd., Nanjing 210035, China Department of Physics, Balikesir University, Balikesir 10145, Turkey |
Author_xml | – sequence: 1 givenname: Hao surname: Wang fullname: Wang, Hao organization: Materials Research Institute, Technical Center of China Tobacco Yunnan Industrial Co., Ltd., State Key Laboratory of Rolling and Automation, Northeastern University – sequence: 2 givenname: Changsheng surname: Li fullname: Li, Changsheng email: lics@ral.neu.edu.cn organization: State Key Laboratory of Rolling and Automation, Northeastern University – sequence: 3 givenname: Jianbo surname: Zhan fullname: Zhan, Jianbo organization: Materials Research Institute, Technical Center of China Tobacco Yunnan Industrial Co., Ltd – sequence: 4 givenname: Zhenhua surname: Yu fullname: Yu, Zhenhua organization: Materials Research Institute, Technical Center of China Tobacco Yunnan Industrial Co., Ltd – sequence: 5 givenname: Yafeng surname: Ji fullname: Ji, Yafeng organization: Engineering Research Center for Department of Heavy Machinery Education, Taiyuan University of Science and Technology – sequence: 6 givenname: Guanglei surname: Wang fullname: Wang, Guanglei organization: Nanjing Iron and Steel Co. Ltd – sequence: 7 givenname: Deniz surname: Perin fullname: Perin, Deniz organization: Department of Physics, Balikesir University |
BookMark | eNp9kEFrFTEQx4O0YFv9AN6CIniJziS72exRS1uFBxa2BW8hm519pmyT12Qf0m9vyisiHiSHhOH3n5n8TtlRTJEYe4PwEQG6TwWx7VsBqAUqY4R-wU6w75WARnVH9Q0AQjaoXrLTUu4AGlBan7AfF_NMfuVp5l_csvDB5zCGuOUp8uv0izLfpFL4QDuX3RpqtZKXJNT7IfCr7EIUKQeKK018CEvwlRhWouUVO57dUuj1833Gbi8vbs6_is33q2_nnzfCK2lWgbLTjW6avtemn9rOSzVNbpZSt3rsTOslKq-Um7Ae3yo5j0DdqDR5pLEndcY-HPrucnrYU1ntfSielsVFSvti0YABrTWqir77B71L-xzrdhY7A00rFZhK4YHyuf4802x3Ody7_GgR7JNre3Btq2v75NrqmpGHTKls3FL-q_N_Qm-fB_1McftQc38maW3aqqTu_BvFlIwF |
Cites_doi | 10.1016/S0304-8853(00)00094-9 10.1016/j.renene.2011.12.002 10.1016/0304-8853(94)90515-0 10.1016/j.epsr.2010.03.003 10.1016/j.jmmm.2006.02.183 10.1016/j.jmmm.2004.02.006 10.1016/j.scriptamat.2012.02.027 10.1016/j.jmmm.2012.09.055 10.1016/S1006-706X(09)60065-0 10.1007/s12613-014-1012-8 10.2355/isijinternational.43.736 10.1016/j.jmmm.2009.08.030 10.1016/j.jmst.2013.03.018 10.1016/S1006-706X(11)60035-6 10.1049/PBPO037E 10.1007/BF02870878 10.1016/j.actamat.2004.10.040 10.1049/PBPO037E_ch3 |
ContentType | Journal Article |
Copyright | Wuhan University of Technology and Springer-Verlag Berlin Heidelberg 2016 |
Copyright_xml | – notice: Wuhan University of Technology and Springer-Verlag Berlin Heidelberg 2016 |
DBID | 2RA 92L CQIGP W92 ~WA AAYXX CITATION 7SR 8AO 8BQ 8FD 8FE 8FG ABJCF AFKRA BENPR BGLVJ CCPQU D1I DWQXO HCIFZ JG9 KB. PDBOC PQEST PQQKQ PQUKI PRINS |
DOI | 10.1007/s11595-016-1388-6 |
DatabaseName | 维普_期刊 中文科技期刊数据库-CALIS站点 维普中文期刊数据库 中文科技期刊数据库-工程技术 中文科技期刊数据库- 镜像站点 CrossRef Engineered Materials Abstracts ProQuest Pharma Collection METADEX Technology Research Database ProQuest SciTech Collection ProQuest Technology Collection Materials Science & Engineering Collection ProQuest Central AUTh Library subscriptions: ProQuest Central Technology Collection ProQuest One Community College ProQuest Materials Science Collection ProQuest Central SciTech Premium Collection Materials Research Database Materials Science Database Materials Science Collection ProQuest One Academic Eastern Edition (DO NOT USE) ProQuest One Academic ProQuest One Academic UKI Edition ProQuest Central China |
DatabaseTitle | CrossRef ProQuest Materials Science Collection Materials Research Database Technology Collection Technology Research Database ProQuest One Academic Eastern Edition Materials Science Collection SciTech Premium Collection ProQuest One Community College ProQuest Technology Collection ProQuest SciTech Collection ProQuest Pharma Collection ProQuest Central China METADEX ProQuest Central Engineered Materials Abstracts ProQuest One Academic UKI Edition ProQuest Central Korea Materials Science & Engineering Collection Materials Science Database ProQuest One Academic |
DatabaseTitleList | ProQuest Materials Science Collection Materials Research Database |
Database_xml | – sequence: 1 dbid: 8FG name: ProQuest Technology Collection url: https://search.proquest.com/technologycollection1 sourceTypes: Aggregation Database |
DeliveryMethod | fulltext_linktorsrc |
Discipline | Engineering |
DocumentTitleAlternate | Effect of Ball Scribing on Power Loss Separation of Fe-3%Si Grain-oriented Silicon Steel |
EISSN | 1993-0437 |
EndPage | 439 |
ExternalDocumentID | 4019822641 10_1007_s11595_016_1388_6 668549913 |
GroupedDBID | -58 -5G -BR -EM -Y2 -~C .86 .VR 06C 06D 0R~ 0VY 188 1N0 29L 2B. 2C0 2J2 2JN 2JY 2KG 2KM 2LR 2RA 2~H 30V 4.4 406 408 40D 40E 5VR 5VS 6NX 8AO 8FE 8FG 8RM 8TC 8UJ 92H 92I 92L 92R 93N 95- 95. 95~ 96X AAAVM AABHQ AAFGU AAHNG AAIAL AAJKR AANZL AARHV AARTL AATNV AATVU AAUYE AAYFA AAYIU AAYQN AAYTO ABDZT ABECU ABFGW ABFTV ABHQN ABJCF ABJNI ABJOX ABKAS ABKCH ABMNI ABMQK ABNWP ABQBU ABSXP ABTEG ABTHY ABTKH ABTMW ABWNU ABXPI ACAOD ACBMV ACBRV ACBXY ACBYP ACGFS ACHSB ACHXU ACIGE ACIPQ ACIWK ACKNC ACMDZ ACMLO ACOKC ACOMO ACSNA ACTTH ACVWB ACWMK ACZOJ ADHHG ADHIR ADINQ ADKNI ADKPE ADMDM ADOXG ADRFC ADTPH ADURQ ADYFF ADZKW AEBTG AEFTE AEGAL AEGNC AEJHL AEJRE AENEX AEOHA AEPYU AESKC AESTI AETLH AEVLU AEVTX AEXYK AFGCZ AFKRA AFLOW AFNRJ AFQWF AFUIB AFWTZ AFZKB AGAYW AGDGC AGGBP AGJBK AGMZJ AGQMX AGWIL AGWZB AGYKE AHAVH AHBYD AHKAY AHSBF AHYZX AIIXL AILAN AIMYW AITGF AJBLW AJDOV AJRNO AKQUC ALMA_UNASSIGNED_HOLDINGS ALWAN AMKLP AMXSW AMYLF AMYQR AOCGG ARMRJ ASPBG AVWKF AXYYD AZFZN B-. BA0 BDATZ BENPR BGLVJ BGNMA CAG CCEZO CCPQU CDRFL CHBEP COF CQIGP CSCUP CW9 CZ9 D1I DDRTE DNIVK DPUIP DU5 EBLON EBS EIOEI EJD ESBYG FA0 FERAY FFXSO FIGPU FINBP FNLPD FRRFC FSGXE FWDCC G-Y G-Z GGCAI GGRSB GJIRD GNWQR GQ6 GQ7 HCIFZ HF~ HG6 HLICF HMJXF HRMNR HZ~ IJ- IKXTQ IWAJR IXD I~X I~Z J-C JBSCW JZLTJ KB. KC. KOV LLZTM M4Y MA- NPVJJ NQJWS NU0 O9- O9J P9N PDBOC PF0 PT4 QOR QOS R89 R9I ROL RPX RSV S16 S1Z S27 S3B SAP SCL SCM SDH SHX SISQX SNE SNPRN SNX SOHCF SOJ SPISZ SQXTU SRMVM SSLCW STPWE SZN T13 TCJ TGT TSG TUC U2A UG4 UGNYK UNUBA UOJIU UTJUX UZXMN VC2 VFIZW W48 W92 WK8 YLTOR Z5O Z7R Z7S Z7V Z7W Z7X Z7Y Z7Z Z85 ZMTXR ~A9 ~WA AACDK AAJBT AASML AAYXX ABAKF ACDTI AEFQL AEMSY AGQEE AGRTI AIGIU CITATION H13 SJYHP 7SR 8BQ 8FD DWQXO JG9 PQEST PQQKQ PQUKI PRINS |
ID | FETCH-LOGICAL-c328t-1276464499689d57c23ddaf22656b785c213c33ad1d1dc532fb0e7b36ec1eb9e3 |
IEDL.DBID | AGYKE |
ISSN | 1000-2413 |
IngestDate | Fri Aug 16 01:45:28 EDT 2024 Thu Oct 10 18:42:48 EDT 2024 Thu Sep 12 17:18:20 EDT 2024 Sat Dec 16 12:02:53 EST 2023 Wed Feb 14 10:20:03 EST 2024 |
IsPeerReviewed | true |
IsScholarly | true |
Issue | 2 |
Keywords | Fe-3%Si grain-oriented silicon steel abnormal loss eddy current loss ball scribing hysteresis loss |
Language | English |
LinkModel | DirectLink |
MergedId | FETCHMERGED-LOGICAL-c328t-1276464499689d57c23ddaf22656b785c213c33ad1d1dc532fb0e7b36ec1eb9e3 |
Notes | Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of power loss,including hysteresis loss,abnormalloss,and eddy current loss,were measured and calculated,respectively.The loss variation and ratio were analyzed based on the experimentaldata.At 1.0 T,hysteresis loss of tested steelwith scribing spacing of 8 mm descends by 8.2% compared to samples without scribing,which is similar to the totalloss variation,and abnormalloss descends by 16.8%.At 1.0 T,hysteresis loss ratio of the steelwith scribing spacing of 16 mm ascends from 55.7% to 57.9%,and eddy current loss increases from 17.4% to 24.1%,while abnormalloss descends from 26.9% to 23.7%.The experimentalresults show that the reduction of power loss after scribing is mainly due to decreasing of hysteresis loss and abnormalloss. 42-1680/TB Fe-3%Si grain-oriented silicon steel ball scribing hysteresis loss eddy current loss abnormal loss ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
PQID | 1780452308 |
PQPubID | 1476361 |
PageCount | 5 |
ParticipantIDs | proquest_miscellaneous_1808066613 proquest_journals_1780452308 crossref_primary_10_1007_s11595_016_1388_6 springer_journals_10_1007_s11595_016_1388_6 chongqing_primary_668549913 |
PublicationCentury | 2000 |
PublicationDate | 2016-04-01 |
PublicationDateYYYYMMDD | 2016-04-01 |
PublicationDate_xml | – month: 04 year: 2016 text: 2016-04-01 day: 01 |
PublicationDecade | 2010 |
PublicationPlace | Wuhan |
PublicationPlace_xml | – name: Wuhan |
PublicationSubtitle | Materials Science Edition |
PublicationTitle | Journal of Wuhan University of Technology. Materials science edition |
PublicationTitleAbbrev | J. Wuhan Univ. Technol.-Mat. Sci. Edit |
PublicationTitleAlternate | Journal of Wuhan University of Technology. Materials Science Edition |
PublicationYear | 2016 |
Publisher | Wuhan University of Technology Springer Nature B.V |
Publisher_xml | – name: Wuhan University of Technology – name: Springer Nature B.V |
References | Weidenfeller, Anhalt (CR8) 2010; 322 Wang, Li, Zhu (CR13) 2013; 26 Kumano, Haratani, Ushigami (CR4) 2003; 43 Snell, Beckley (CR12) 1994; 133 Broddefalk, Lindenmo (CR18) 2006; 304 Bottauscio, Chiampi, Chiarabaglio (CR3) 2000; 215-216 Moses (CR6) 2012; 67 Zhmetko (CR10) 2004; 279 Boglietti, Cavagnino (CR14) 2010; 80 Bülow, Eriksson, Bernhoff (CR17) 2012; 43 Gheorghies, Doniga (CR9) 2009; 16 Li, Yang, Wang (CR2) 2011; 18 Beckley (CR11) 2002 Kollár, Füzer (CR16) 2013; 237 Wang, Li, Zhu (CR15) 2013; 29 Wang, Li, Huo (CR19) 2013; 20 Wang, Li, Zhu (CR7) 2014; 21 Hu, Zhang, Zhang (CR1) 2005; 20 Imafuku, Suzuki, Akita (CR5) 2005; 53 T Kumano (1388_CR4) 2003; 43 D Snell (1388_CR12) 1994; 133 B Weidenfeller (1388_CR8) 2010; 322 A Broddefalk (1388_CR18) 2006; 304 AJ Moses (1388_CR6) 2012; 67 CS Li (1388_CR2) 2011; 18 M Imafuku (1388_CR5) 2005; 53 P Beckley (1388_CR11) 2002 C Gheorghies (1388_CR9) 2009; 16 D N Zhmetko (1388_CR10) 2004; 279 H Wang (1388_CR13) 2013; 26 P Kollár (1388_CR16) 2013; 237 O Bottauscio (1388_CR3) 2000; 215-216 H Wang (1388_CR15) 2013; 29 CZ Hu (1388_CR1) 2005; 20 H Wang (1388_CR7) 2014; 21 A Boglietti (1388_CR14) 2010; 80 H Wang (1388_CR19) 2013; 20 F Bülow (1388_CR17) 2012; 43 |
References_xml | – volume: 20 start-page: 99 issue: 3 year: 2013 end-page: 103 ident: CR19 article-title: Effect of Ball Scribing on Iron Loss of CGO and HGO Electrical Steel[J] publication-title: J. Harbin Inst. Technol. (New Series) contributor: fullname: Huo – volume: 215-216 start-page: 130 issue: 2 year: 2000 end-page: 132 ident: CR3 article-title: Use of Grain-oriented Materials in Low-frequency Magnetic Shielding[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/S0304-8853(00)00094-9 contributor: fullname: Chiarabaglio – volume: 43 start-page: 389 issue: 3 year: 2012 end-page: 392 ident: CR17 article-title: No-load Core Loss Prediction of PM Generator at Low Electrical Frequency[J] publication-title: Renewable Energy doi: 10.1016/j.renene.2011.12.002 contributor: fullname: Bernhoff – volume: 133 start-page: 167 issue: 1-3 year: 1994 end-page: 169 ident: CR12 article-title: Domain Refinement of High-permeability Grainoriented Electrical Steel Using Low-friction Ball Units[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/0304-8853(94)90515-0 contributor: fullname: Beckley – volume: 80 start-page: 1121 issue: 6 year: 2010 end-page: 1127 ident: CR14 article-title: Iron Loss Prediction with PWM Supply: An Overview of Proposed Methods from an Engineering Application Point of View[J] publication-title: Electr. Power Syst. Res. doi: 10.1016/j.epsr.2010.03.003 contributor: fullname: Cavagnino – volume: 304 start-page: e586 issue: 3 year: 2006 end-page: e588 ident: CR18 article-title: Dependence of the Power Losses of a Nonoriented 3% Si-steel on Frequency and Gauge[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2006.02.183 contributor: fullname: Lindenmo – volume: 279 start-page: 375 issue: 2-3 year: 2004 end-page: 388 ident: CR10 article-title: The Dynamics of the Sandwich Domain Structure in 3%Si-Fe Sheets[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2004.02.006 contributor: fullname: Zhmetko – volume: 67 start-page: 560 issue: 6 year: 2012 end-page: 565 ident: CR6 article-title: Energy Efficient Electrical Steels: Magnetic Performance Prediction and Optimization[J] publication-title: Scr. Mater. doi: 10.1016/j.scriptamat.2012.02.027 contributor: fullname: Moses – volume: 237 start-page: 146 issue: 2 year: 2013 end-page: 150 ident: CR16 article-title: Power Loss Separation in Febased Composite Materials[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2012.09.055 contributor: fullname: Füzer – volume: 16 start-page: 78 issue: 4 year: 2009 end-page: 83 ident: CR9 article-title: Evolution of Texture in Grain Oriented Electrical Steels[J] publication-title: J. Iron. Steel Res. Int. doi: 10.1016/S1006-706X(09)60065-0 contributor: fullname: Doniga – volume: 21 start-page: 1077 issue: 11 year: 2014 end-page: 1082 ident: CR7 article-title: Hard Magnetization Direction and its Relation with Magnetic Permeability of Highly Grain-oriented Electrical Steel[J] publication-title: Int. J. Miner. Metall. Mater. doi: 10.1007/s12613-014-1012-8 contributor: fullname: Zhu – volume: 26 start-page: 420 issue: 6 year: 2013 end-page: 426 ident: CR13 article-title: Effect of Ball Scribing on Relative Permeability of Grain-oriented Electrical Steel[J] publication-title: Acta Metall. Sinica contributor: fullname: Zhu – volume: 43 start-page: 736 issue: 5 year: 2003 end-page: 745 ident: CR4 article-title: The Improvement of Primary Texture for Sharp Goss Orientation on Grain Oriented Silicon Steel[J] publication-title: ISIJ Int. doi: 10.2355/isijinternational.43.736 contributor: fullname: Ushigami – volume: 322 start-page: 69 issue: 1 year: 2010 end-page: 72 ident: CR8 article-title: Effect of Laser Treatment on High and Low Induction Loss Components of Grain Oriented Iron-silicon Sheets[J] publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2009.08.030 contributor: fullname: Anhalt – volume: 29 start-page: 673 issue: 7 year: 2013 end-page: 677 ident: CR15 article-title: Effect of Ball Scribing on Magnetic Barkhausen Noise of Grain-oriented Electrical Steel[J] publication-title: J. Mater. Sci. Technol. doi: 10.1016/j.jmst.2013.03.018 contributor: fullname: Zhu – volume: 18 start-page: 40 issue: 3 year: 2011 end-page: 46 ident: CR2 article-title: Texture of Cold Rolled Strip for Fe-3Si Steel Produced by Thin Slab Casting and Rolling[J] publication-title: J. Iron. Steel Res. Int. doi: 10.1016/S1006-706X(11)60035-6 contributor: fullname: Wang – start-page: 19 year: 2002 end-page: 30 ident: CR11 publication-title: Electrical Steels for Rotating Machines[M] doi: 10.1049/PBPO037E contributor: fullname: Beckley – volume: 20 start-page: 72 issue: 1 year: 2005 end-page: 74 ident: CR1 article-title: Fabrication of Fe-6. 5wt% Si Bulk by Spark Plasma Sintering[J] publication-title: J. Wuhan Univ. Technol. -Mater. Sci. Ed. doi: 10.1007/BF02870878 contributor: fullname: Zhang – volume: 53 start-page: 939 issue: 4 year: 2005 end-page: 945 ident: CR5 article-title: Effects of Laser Irradiation on Iron Loss Reduction for Fe–3%Si Grain-oriented Silicon Steel[J] publication-title: Acta Mater. doi: 10.1016/j.actamat.2004.10.040 contributor: fullname: Akita – volume: 29 start-page: 673 issue: 7 year: 2013 ident: 1388_CR15 publication-title: J. Mater. Sci. Technol. doi: 10.1016/j.jmst.2013.03.018 contributor: fullname: H Wang – volume: 18 start-page: 40 issue: 3 year: 2011 ident: 1388_CR2 publication-title: J. Iron. Steel Res. Int. doi: 10.1016/S1006-706X(11)60035-6 contributor: fullname: CS Li – volume: 237 start-page: 146 issue: 2 year: 2013 ident: 1388_CR16 publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2012.09.055 contributor: fullname: P Kollár – volume: 43 start-page: 389 issue: 3 year: 2012 ident: 1388_CR17 publication-title: Renewable Energy doi: 10.1016/j.renene.2011.12.002 contributor: fullname: F Bülow – volume: 304 start-page: e586 issue: 3 year: 2006 ident: 1388_CR18 publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2006.02.183 contributor: fullname: A Broddefalk – volume: 53 start-page: 939 issue: 4 year: 2005 ident: 1388_CR5 publication-title: Acta Mater. doi: 10.1016/j.actamat.2004.10.040 contributor: fullname: M Imafuku – volume: 215-216 start-page: 130 issue: 2 year: 2000 ident: 1388_CR3 publication-title: J. Magn. Magn. Mater. doi: 10.1016/S0304-8853(00)00094-9 contributor: fullname: O Bottauscio – volume: 133 start-page: 167 issue: 1-3 year: 1994 ident: 1388_CR12 publication-title: J. Magn. Magn. Mater. doi: 10.1016/0304-8853(94)90515-0 contributor: fullname: D Snell – volume: 67 start-page: 560 issue: 6 year: 2012 ident: 1388_CR6 publication-title: Scr. Mater. doi: 10.1016/j.scriptamat.2012.02.027 contributor: fullname: AJ Moses – volume: 279 start-page: 375 issue: 2-3 year: 2004 ident: 1388_CR10 publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2004.02.006 contributor: fullname: D N Zhmetko – volume: 20 start-page: 99 issue: 3 year: 2013 ident: 1388_CR19 publication-title: J. Harbin Inst. Technol. (New Series) contributor: fullname: H Wang – volume: 16 start-page: 78 issue: 4 year: 2009 ident: 1388_CR9 publication-title: J. Iron. Steel Res. Int. doi: 10.1016/S1006-706X(09)60065-0 contributor: fullname: C Gheorghies – volume: 26 start-page: 420 issue: 6 year: 2013 ident: 1388_CR13 publication-title: Acta Metall. Sinica contributor: fullname: H Wang – start-page: 19 volume-title: Electrical Steels for Rotating Machines[M] year: 2002 ident: 1388_CR11 doi: 10.1049/PBPO037E_ch3 contributor: fullname: P Beckley – volume: 43 start-page: 736 issue: 5 year: 2003 ident: 1388_CR4 publication-title: ISIJ Int. doi: 10.2355/isijinternational.43.736 contributor: fullname: T Kumano – volume: 20 start-page: 72 issue: 1 year: 2005 ident: 1388_CR1 publication-title: J. Wuhan Univ. Technol. -Mater. Sci. Ed. doi: 10.1007/BF02870878 contributor: fullname: CZ Hu – volume: 21 start-page: 1077 issue: 11 year: 2014 ident: 1388_CR7 publication-title: Int. J. Miner. Metall. Mater. doi: 10.1007/s12613-014-1012-8 contributor: fullname: H Wang – volume: 322 start-page: 69 issue: 1 year: 2010 ident: 1388_CR8 publication-title: J. Magn. Magn. Mater. doi: 10.1016/j.jmmm.2009.08.030 contributor: fullname: B Weidenfeller – volume: 80 start-page: 1121 issue: 6 year: 2010 ident: 1388_CR14 publication-title: Electr. Power Syst. Res. doi: 10.1016/j.epsr.2010.03.003 contributor: fullname: A Boglietti |
SSID | ssj0040366 |
Score | 2.05161 |
Snippet | Power loss of Fe-3%Sigrain-oriented silicon steelwas measured after ballscribing with different spacing using a self-designed tool.Three different sections of... Power loss of Fe-3%Si grain-oriented silicon steel was measured after ball scribing with different spacing using a self-designed tool. Three different sections... |
SourceID | proquest crossref springer chongqing |
SourceType | Aggregation Database Publisher |
StartPage | 435 |
SubjectTerms | Chemistry and Materials Science Eddy current testing Electrical steels Hysteresis losses Materials Science Mathematical analysis Metallic Materials Power loss Separation Silicon steels Steels 低功率损耗 分离效果 功率损失 取向硅钢 实验数据分析 涡流损耗 磁滞损耗 线间距 |
SummonAdditionalLinks | – databaseName: AUTh Library subscriptions: ProQuest Central dbid: BENPR link: http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwfV1bS8MwFA66veiDeMW5KRH0RQmuTdPLk6hsDMEh6mBvJUnTOSjtZrf_7zm9bFNQ-taGhOacnHu-Q8iV64AaF76CIy4DcFCMz0AtSCZj1RWx48iuwdDAy9AdjJznsRhXAbe8KqusZWIhqKNMY4z8zkKkHAxh-vezOcOuUZhdrVpobJOmbTmYpm0-9oavb7UsdkA-F_eL8P40ZpDqvGZxeQ40ORauFTh8PivQFT6zdDIHnfFTS61Nz1_Z0kIJ9ffJXmU90oeS3Adky6SHZHcDU_CIjEs8YprFVMkkoSgWwPud0CylM2yJRhNYkeamBP2GtzCybxi_fp_SCTaMwN9GpM6I5tMEGCWlwAkmOSajfu_jacCq9glMc9tfMMv2XAfMHfBo_CASnrZ5FMkY7C3hKs8X2ra45lxGFjxacBvIYzzFXaMtowLDT0gjzVJzSqgAQ8WgL6OVdrwoUpyrAEwbg8Ci0rgt0l5tXTgrYTJC1_XR-bR4i9zUm7n6uEZLRiqEWGeGVAhhqk693WF1nPJwTfwWuVx9hoOA2Q2ZmmwJYxAhE5wxXO-2JtPGFH8tePb_gm2yYyOPFMU6HdJYfC3NOdghC3VRMds3cmXXcQ priority: 102 providerName: ProQuest |
Title | Effect of Ball Scribing on Power Loss Separation of Fe-3%Si Grain-oriented Silicon Steel |
URI | http://lib.cqvip.com/qk/84253X/201602/668549913.html https://link.springer.com/article/10.1007/s11595-016-1388-6 https://www.proquest.com/docview/1780452308 https://search.proquest.com/docview/1808066613 |
Volume | 31 |
hasFullText | 1 |
inHoldings | 1 |
isFullTextHit | |
isPrint | |
link | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwlV1Lb9swDCbS9LIe9i6WJQtUoL1scFBblqwcsyFpsaLF0C1AdjIkWcmKGHa2JJf9-pF-JXsdAh8MSIIEiZRIiuQngHMZohgXyuAW10M0UJzyUCxoT8_NpZiHob50dDVweyevp-HHmZi1IGiuLrLloPZIFgf1LtcNBS_FmRWwecqTR3AsCO-rDcejq6834_r8DfFMLnKKKGeavEa1L_NfnRCiwrc8W3zHAX-XTDt18w8PaSF4Jk_KZMB1gVdI8SbLwXZjBvbn32iOB8zpKTyu9FA2KhnnGbRc9hxO9tAJX8CsRDZm-ZwZnaaMDhi0oxcsz9iKHldjKc6DrV0JH46l2HLiPH7x-YEt6OkJLycUZdRp2fohRZbLGPKUS1_CdDL-8uHaqx5i8CwP1Mbzg0iGqDihbaSGiYhswJNEz1FzE9JEStjA55Zznfj4WcEDJLSLDJfO-s4MHT-FdpZn7hUwgSqPI6vIGhtGSWI4N0NUkhxBlGonO9BtCBKvSsCNWEpFZqzPO_C2JlFTucNdpsWMKWKNFjPGrno1EeNqY65jnwCX6CZcdeCsqcYtRX4Snbl8i20IaxPNOhrvXU24vS7-N-Drg1p34VFAlC-igHrQ3vzYujeo4GxMH47U5Kpf8TX-34_vPt1j6TQY_QIEvPID |
link.rule.ids | 315,786,790,12792,21416,27955,27956,33406,33407,33777,33778,41114,41556,42183,42625,43633,43838,52144,52267 |
linkProvider | Springer Nature |
linkToHtml | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwfV3NT8IwFG8UD-rB-BkR1JroRbPI1q0rJ2OMExW4CAm3pe0KkiwbOPj_fW9sgCaa3bamzfpe33d_j5Br7oIa94SCIy6b4KAYYYFakJYcqoY3dF3ZMBga6HR5q---DbxBEXDLirLKUibmgjpKNcbI721EysEQpniYTC3sGoXZ1aKFxibZchlnyOcieCklsQvSOb9dhLenMX9UZjXzq3Ogx7FsLUfhE1aOrfCZJqMpaIyfOmpleP7KleYqKNgne4XtSB8XxD4gGyY5JLtriIJHZLBAI6bpkCoZxxSFAvi-I5omdIIN0WgMK9LMLCC_4S2MDIzFbj7GdITtIvCnEaczotk4BjZJKPCBiY9JP3juPbWsonmCpZkjZpbt-NwFYwf8GdGMPF87LIrkEKwtjytfeNqxmWZMRjY82mMOEMf4inGjbaOahp2QSpIm5pRQD8wUg56MVtr1o0gxpppg2BiEFZWGV0ltuXXhZAGSEXIu0PW0WZXclpu5_LjCSkYqhFhlhlQIYap6ud1hcZiycEX6KrlafoZjgLkNmZh0DmMQHxNcMVzvriTT2hR_LXj2_4KXZLvV67TD9mv3vUZ2HOSXvGynTiqzr7k5B4tkpi5ytvsG_dXY-A |
linkToPdf | http://utb.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwpV3dT9swED-NIiF42AYDUSjDSPDClEJix0kfq0HHt5AAqXsKtuMURJSUNX3ZX7-7JmkZ2h4Qylti2bHv7Lvz3f0OYFcKFON-qHGLqw4aKDZ0UCwoRyX60E-EUIeWrgYur-TJnTjr-_2qzumojnavXZJlTgOhNGXFwTBODmaJbyiFKehsgqEXOnIO5gXuWtGA-e6Pn-fH9WEs8ICeJBhRAjW5kGrH5r86IXiFhzwbPOPgf4upme75yl06kUK9T3Bf_38ZfPLUHhe6bX6_gnZ8xwQ_w8dKQ2XdkqWW4YPNVmDpBW7hF-iXmMcsT5hWacro6EELe8DyjA2p7BpLcVJsZEtgcXyLLXvW4Xs3j2xARSmcnPCVUdtlo8cUmTFjyG02XYW73vHt9xOnKtHgGO6FheN6gRSoUqHVFHZiPzAej2OVoE7nSx2EvvFcbjhXsYuP8bmHLGADzaU1rtUdy9egkeWZXQfmozJkyV4y2oggjjXnuoPqkyXwUmVlEzan1ImGJRRHJGVIBq7Lm7Bf02v6cYbITIsZUSwbLWaEXbVqikbVlh1FLkEx0R152ISd6WfcbORBUZnNx9iGUDjR4KPxvtVEfNHF_wbceFPrbVi4PupFF6dX55uw6BETTEKFWtAofo3tFmpBhf5acfofkiP7SQ |
openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Ajournal&rft.genre=article&rft.atitle=Effect+of+ball+scribing+on+power+loss+separation+of+Fe-3%25Si+grain-oriented+silicon+steel&rft.jtitle=Journal+of+Wuhan+University+of+Technology.+Materials+science+edition&rft.au=Wang%2C+Hao&rft.au=Li%2C+Changsheng&rft.au=Zhan%2C+Jianbo&rft.au=Yu%2C+Zhenhua&rft.date=2016-04-01&rft.pub=Wuhan+University+of+Technology&rft.issn=1000-2413&rft.eissn=1993-0437&rft.volume=31&rft.issue=2&rft.spage=435&rft.epage=439&rft_id=info:doi/10.1007%2Fs11595-016-1388-6&rft.externalDocID=10_1007_s11595_016_1388_6 |
thumbnail_s | http://utb.summon.serialssolutions.com/2.0.0/image/custom?url=http%3A%2F%2Fimage.cqvip.com%2Fvip1000%2Fqk%2F84253X%2F84253X.jpg |