Fabrication and characterization of the normally,off N-channel lateral 4H-SiC metal-oxide-semiconductor field-effect transistors

In this paper, the normally-off N-channel lateral 4H-SiC metal-oxide-semiconductor field-effect transistors （MOSF- FETs） have been fabricated and characterized. A sandwich- （nitridation-oxidation-nitridation） type process was used to grow the gate dielectric film to obtain high channel mobility. The...

Full description

Saved in:
Bibliographic Details
Published inChinese physics B Vol. 25; no. 3; pp. 362 - 365
Main Author 宋庆文 汤晓燕 何艳静 唐冠男 王悦湖 张艺蒙 郭辉 贾仁需 吕红亮 张义门 张玉明
Format Journal Article
LanguageEnglish
Published 01.03.2016
Subjects
4H-SiC
Breakdown
C-V曲线
Channels
Density
Dielectrics
Field effect transistors
Hysteresis
N沟道
Oxides
Semiconductor devices
制备
场效应迁移率
碳化硅
表征
金属氧化物半导体场效应晶体管
Online AccessGet full text

Cover

More Information
Summary:In this paper, the normally-off N-channel lateral 4H-SiC metal-oxide-semiconductor field-effect transistors （MOSF- FETs） have been fabricated and characterized. A sandwich- （nitridation-oxidation-nitridation） type process was used to grow the gate dielectric film to obtain high channel mobility. The interface properties of 4H-SiC/SiO2 were examined by the measurement of HF l-V, G-V, and C-V over a range of frequencies. The ideal C-V curve with little hysteresis and the frequency dispersion were observed. As a result, the interface state density near the conduction band edge of 4H-SiC was reduced to 2 x 1011 eV-l.cm-2, the breakdown field of the grown oxides was about 9.8 MV/cm, the median peak field- effect mobility is about 32.5 cm2.V-1 .s-1, and the maximum peak field-effect mobility of 38 cm2-V-1 .s-1 was achieved in fabricated lateral 4H-SiC MOSFFETs.
Bibliography:metal-oxide-semiconductor field-effect transistors, 4H-SiC, field-effect mobility, oxidation pro-cess
11-5639/O4
In this paper, the normally-off N-channel lateral 4H-SiC metal-oxide-semiconductor field-effect transistors （MOSF- FETs） have been fabricated and characterized. A sandwich- （nitridation-oxidation-nitridation） type process was used to grow the gate dielectric film to obtain high channel mobility. The interface properties of 4H-SiC/SiO2 were examined by the measurement of HF l-V, G-V, and C-V over a range of frequencies. The ideal C-V curve with little hysteresis and the frequency dispersion were observed. As a result, the interface state density near the conduction band edge of 4H-SiC was reduced to 2 x 1011 eV-l.cm-2, the breakdown field of the grown oxides was about 9.8 MV/cm, the median peak field- effect mobility is about 32.5 cm2.V-1 .s-1, and the maximum peak field-effect mobility of 38 cm2-V-1 .s-1 was achieved in fabricated lateral 4H-SiC MOSFFETs.
ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
ISSN:1674-1056
2058-3834
1741-4199
DOI:10.1088/1674-1056/25/3/037306