Effects of High Temperature and Different Salt Solutions on Basalt Fiber-Reinforced Composites’ Bonded Joint Durability Impact - Peng, Han; Lin, Yinghao; Chen, Zeshao; Ma, Shengtao; Shangguan, Linjian; Cheng, Ruixue; Fan, Yisa (Coatings (Basel), 2023)
Keywords: Adhesives; Aging; Aluminum; Automobiles; Basalt; Bond strength; Bonded joints; Chemical damage; Chemical properties; Composite materials; Curing; Deionization; Durability; Energy consumption; Epoxy resins; Failure modes; Fiber composites; Fiber reinforced polymers; Functional groups; Glass transition temperature; High temperature; High temperature effects; Industrial development; Lap joints; Load; Manufacturing; Mechanical properties; Moisture content; Moisture effects; Saline solutions; Shear strength; Sodium chloride; Stress concentration; Tensile strength; Tensile tests; Thermogravimetric analysis; Water absorption; Water chemistry; Water damage; China